Method for spin coating a surface of an optical article

1. A method for spin coating a surface of an optical article, comprising:

selecting as said optical article an article ( 10 ) with a concave face ( 12 ) able to adopt a facing up position with an edge ( 15 ) at an uppermost portion of the concave face ( 12 ), and selecting said concave face ( 12 ) as said surface to be coated;

dispensing a predetermined volume of a coating solution on said concave face ( 12 ), said coating solution being dispensed only to an area along an entirety of said edge ( 15 ), said concave face ( 12 ) facing up and said coating solution being dispensed to said edge ( 15 ) in a top down manner;

immediately after said dispensing step, waiting with no motion of said article ( 10 ) for said coating solution to flow on said concave face ( 12 ) until said coating solution collects at a location at a center of the concave face ( 12 ); and

after said waiting step, spinning said article ( 10 ) to force the coating solution back to the edge ( 15 ) of the concave face ( 12 ).

2. The method according to claim 1 , wherein no coating solution is dispensed during and after said waiting step.

3. The method according claim 1 , further comprising:

after said step of spinning, flipping said article ( 10 ) so that said concave face ( 12 ) coated with said coating solution ( 18 ) faces down.

4. The method according claim 1 , wherein said coating solution has a viscosity in the range of 1 to 100 cp at 25° C.

5. The method according claim 4 , wherein said coating solution is selected from the group of solutions of primer layer latex comprising functions selected from the group consisting of urethane, (meth)acrylic and butadiene, solutions of liquid crystal material and solutions of polarizing material.

6. The method according claim 5 , wherein said coating solution is a solution of primer layer latex made of an aqueous dispersion of polyurethane.

7. The method according claim 1 , wherein the coating solution ( 18 ) is thermally curable.

8. The method according claim 1 , wherein, during said dispensing step, a relative motion between the optical article ( 10 ) and a nozzle ( 17 ) dispensing said coating solution is less than 100 rpm.

9. The method according claim 8 , wherein during dispensing step, the optical article ( 10 ) is rotating.

10. The method according claim 1 , wherein the duration of the waiting step is in the range of 2 to 10 seconds.

11. The method according claim 1 , wherein, during said spinning step, the speed of rotation of the optical article ( 10 ) is in the range of 100 to 1000 rpm.

12. The method according claim 1 , wherein said edge ( 15 ) is circular.

13. The method according claim 1 , wherein said edge ( 15 ) has a maximum cross dimension within the range of 65 mm to 80 mm.

14. The method according claim 1 , wherein said concave face ( 12 ) has local radii of curvature within the range of 45 mm to 120 mm.

15. The method according claim 2 , further comprising:

after said step of spinning, flipping said article ( 10 ) so that said concave face ( 12 ) coated with said coating solution ( 18 ) faces down.

16. The method according claim 2 , wherein said coating solution has a viscosity in the range of 1 to 100 cp at 25° C.

17. The method according claim 2 , wherein the coating solution ( 18 ) is thermally curable.

18. The method according claim 12 , wherein, during dispensing step, a relative motion between the optical article ( 10 ) and a nozzle ( 17 ) dispensing said coating solution is less than 100 rpm.

19. The method according claim 2 , wherein the duration of the waiting step is in the range of 2 to 10 seconds.

20. The method according claim 2 , wherein, during said spinning step, the speed of rotation of the optical article ( 10 ) is in the range of 100 to 1000 rpm.