Zinc containing glasses and enamels

1. An opaque, fired enamel composition that is lead-free, cadmium-free, bismuth-free, tantalum-free and antimony-free, the enamel composition comprising, prior to firing an organic vehicle and a solids portion, wherein the solids portion comprises a frit portion, wherein the frit portion comprises, prior to firing:

a. 10-80 wt % of a glass frit, the frit comprising

i. 39.74 to 47.72 wt % SiO 2 ,

ii. 12.7 to 22.56 wt % B 2 O 3 ,

iii. 8.89 to 12.73 wt % TiO 2 ,

iv. 0.54 to 13.36 wt % ZnO,

v. 1.72 to 2.17 wt % Li 2 O

vi. 0.67 to 17.57 wt % K 2 O, and

vii. 3.08 to 4.02 wt % F,

viii. 0.58 to 1.41 wt % Al 2 O 3 ,

ix. 0 to 1.27 wt % ZrO 2 ,

x. 0 to 12.01 wt % Na 2 O,

b. a separate and distinct addition of 0.1-30 wt % pigment, and

c. 0.1-15 wt % of a crystalline material selected from the group consisting of zinc borates, zinc silicates, zinc titanates, aluminum silicates, and combinations thereof,

wherein, after firing, the enamel composition exhibits performance of chemical durability against wet through deterioration of at least 24 hours when tested in 0.1N H 2 SO 4 at 80° C.

2. The enamel of claim 1 further comprising (d) 0.1 to 5 wt % of a metal.

3. The enamel composition of claim 1 , wherein the frit portion further comprises sulfur or a metallic sulfide, or combinations thereof, so as to provide an amount of sulfur to the frit portion not exceeding 4 wt %, all percentages prior to firing.

4. The enamel composition of claim 1 , wherein the frit portion further comprises at least one selected from the group consisting of: (a) 0.1-2 wt % Cs 2 O, (b) 0.1-5 wt % MgO, (c) 0.1-5 wt % CeO 2 , (d) 0.1-10 wt % MnO, (e) 0.1-5 wt % CuO, (f) 0.1-5 wt % NiO, (g) 0.1-10 wt % SnO, (h) 0.1-5 wt % P 2 O 5 , (i) 0.1-10 wt % V 2 O 5 , (j) 0.1-5 wt % La 2 O 3 , (k) 0.1-5 wt % Pr 2 O 3 , (l) 0.1-5 wt % Y 2 O 3 , (m) 0.1-5 wt % In 2 O 3 , (n) 0.1-10 wt % Fe 2 O 3 , (O) 0.1-5 wt % Cr 2 O 3 , (q) 0.1-5 wt % CoO, (q) 0.1-4 wt % Nb 2 O 5 , (r) 0.1-4 wt % WO 3 , (s) 0.1-4 wt % MoO 3 , and combinations thereof.

5. The opaque, fired enamel composition of claim 1 , wherein the enamel composition has a minimum firing temperature of no greater than 1250° F.

6. The opaque, fired enamel composition of claim 1 , wherein the enamel composition has a minimum firing temperature of no greater than 1180° F.

7. The enamel composition of claim 2 , further comprising a reducing compound to reduce the metal in the composition or prevent oxidation of metals in the enamel composition to control silver migration into the substrate.

8. The enamel composition of claim 7 , wherein the reducing compounds are selected from the group consisting of silicon metal, zinc sulfide, metallic sulfides, and combinations thereof.

9. A substrate bearing a fired coating, the coating having a minimum firing temperature of no greater than 1180° F., wherein the fired coating comprises a frit portion, said frit portion comprising, prior to firing,

a. 39.74 to 47.72 wt % SiO 2 ,

b. 12.7 to 22.56 wt % B 2 O 3 ,

c. 8.89 to 12.73 wt % TiO 2 ,

d. 0.54 to 13.36 wt % ZnO,

e. 1.72 to 2.17 wt % Li 2 O

f. 0.67 to 17.57 wt % K 2 O, and

g. 3.08 to 4.02 wt % F,

h. 0.58 to 1.41 wt % Al 2 O 3 ,

i. 0 to 1.27 wt % ZrO 2 , and

j. 0 to 12.01 wt % Na 2 O,

the fired coating exhibiting performance of chemical durability against wet through deterioration of at least 24 hours when tested in 0.1N H 2 SO 4 at 80° C.