Anchored nanostructure materials and method of fabrication
View Patent ↗Anchored nanostructure materials and methods for their fabrication are described. The anchored nanostructure materials may utilize nano-catalysts that include powder-based or solid-based support materials. The support material may comprise metal, such as NiAl, ceramic, a cermet, or silicon or other metalloid. Typically, nanoparticles are disposed adjacent a surface of the support material. Nanostructures may be formed as anchored to nanoparticles that are adjacent the surface of the support material by heating the nano-catalysts and then exposing the nano-catalysts to an organic vapor. The nanostructures are typically single wall or multi-wall carbon nanotubes.
1. A method of producing anchored carbon nanotubes comprising:
(a) etching a substrate comprising a metal selected from the group consisting of scandium, titanium, vanadium, chromium, manganese, iron, cobalt, nickel, copper, and zinc with an etchant selected from the group consisting of an aqueous solution of an aluminum salt, a dilute acid, and a combination thereof, wherein metal ions from the substrate form in the etchant;
(b) drying the substrate in the presence of the etchant, wherein nano-size deposits comprising the metal ions are deposited adjacent the surface of the substrate;
(c) exposing the metal ions to hydrogen to reduce the metal ions and produce nano-catalysts; and
(d) in a step that is separate from step (c), exposing the nano-catalysts to an organic gas to grow carbon nanotubes on the nano-catalysts, forming the anchored carbon nanotubes.
2. The method of claim 1 wherein the substrate comprises nickel and wherein the etchant is selected from the group consisting of an aqueous solution of a chloride salt of aluminum, dilute hydrochloric acid, and combinations thereof.
3. The method of claim 1 wherein the substrate comprises nickel and wherein the etchant is selected from the group consisting of an aqueous solution of a nitrate salt of aluminum, dilute nitric acid, and combinations thereof.
4. The method of claim 1 wherein step (d) further comprises exposing the nano-catalysts to hydrogen.
5. The method of claim 1 wherein the substrate comprises nickel in the form of nickel aluminide and wherein the etchant is selected from the group consisting of an aqueous solution of a chloride salt of aluminum, dilute hydrochloric acid, and combinations thereof.
6. The method of claim 1 wherein the substrate comprises nickel in the form of nickel aluminide and wherein the etchant is selected from the group consisting of an aqueous solution of a nitrate salt of aluminum, dilute nitric acid, and combinations thereof.
7. The method of claim 1 further comprising disposing a coupling agent on the surface of the substrate to facilitate binding of the metal ions to the substrate.
8. The method of claim 1 further comprising disposing a chelating agent on the surface of the substrate to facilitate binding of the metal ions to the substrate.