ADHESIVE FILM WITH HIGH OPTICAL TRANSPERANCY, AS AN ANTI-SPLINTER COVER FOR ADHERING TO GLASS WINDOWS IN ELECTRONIC COMPONENTS FOR CONSUMER ITEMS
The invention relates to an adhesive film comprising at least one carrier film and at least one layer of an adhesive material. The invention is characterised in that the carrier film has a tensile strength of at least 50 MPa, measured according to ASTM D882, a haze value of no more than 3%, measured according to ASTM D1003, and a transmission of at least 80%, measured according to ASTM D1003, in light with a wavelength of 550 nm; and in that the adhesive film has a transmission of at least 70%, measured according to ASTM D1003. The invention also relates to the use of a corresponding single-sided or double-sided adhesive film, as an anti-splinter cover for glass windows, especially for electronic consumer items.
1 . A pressure-sensitive adhesive film comprising at least one carrier film and at least one layer of a pressure-sensitive adhesive, wherein the carrier film possesses:
a tensile strength of at least 50 MPa, measured according to ASTM D882,
a haze value of not more than 3%, measured according to ASTM D1003, and
a transmittance for light with a wavelength of 550 nm of at least 80%, measured according to ASTM D1003,
and in that the pressure-sensitive adhesive film possesses
a transmittance of at least 70%, measured according to ASTM D1003.
2 . The pressure-sensitive adhesive film of claim 1 , wherein the haze value of the carrier film is not more than 2%, measured according to ASTM D1003.
3 . The pressure-sensitive adhesive film of claim 1 , wherein the carrier film possesses a refractive index of at least 1.48.
4 . The pressure-sensitive adhesive film of claim 1 , wherein the pressure-sensitive adhesive is based on polyacrylates and/or polymethacrylates.
5 . The pressure-sensitive adhesive film of claim 1 , wherein the pressure-sensitive adhesive has a refractive index of 1.43 (25° C.; λ=550 nm±150 nm).
6 . The pressure-sensitive adhesive film of claim 1 , wherein the pressure-sensitive adhesive is based on acrylate block copolymers.
7 . The pressure-sensitive adhesive film of claim 1 , wherein the pressure-sensitive adhesive is based on silicone rubbers.
8 . The pressure-sensitive adhesive film of claim 1 , wherein the pressure-sensitive adhesive has a refractive index of 1.52 (25° C.; λ=550 nm±150 nm).
9 . An assembly composed of a pressure-sensitive adhesive film of claim 1 and a glass sheet on the side of the layer of pressure-sensitive adhesive that is facing away from the carrier film.
10 . A method of protecting a glass sheet from splintering, said method comprising adhering to said glass sheet a single-sided or double-sided pressure-sensitive adhesive film of claim 1 .