Process and apparatus for producing propylene
View Patent ↗A process for producing propylene, which including feeding at least one of dimethyl ether and methanol to a reactor to be reacted in the presence of a catalyst; supplying an obtained reaction product to a separator by which low-boiling compounds having a boiling point of −50° C. or lower at atmospheric pressure among the reaction product are separated; and recycling a proportion of at least 70% of a total amount of the separated low-boiling compounds to said reactor.
1. A process for producing propylene, comprising the steps of:
feeding at least one of dimethyl ether and methanol to a reactor to be reacted in the presence of a catalyst;
supplying an obtained reaction product to a separator by which low-boiling compounds having a boiling point of −50° C. or lower at atmospheric pressure among the reaction product are separated;
recycling at least 90% of a total amount of the separated low-boiling compounds to said reactor;
converting at least a portion of the remainder of the separated low-boiling compounds to a C 4 ˜C 10 hydrocarbon;
recycling the C 4 ˜C 10 hydrocarbon to said reactor; and
maintaining a partial pressure of at least one of dimethyl and methanol in the reactor at 0.005 MPa-0.20 MPa.
2. The process according to claim 1 , wherein at least a part of C 4 ˜C 6 hydrocarbons separated by the separator are recycled to the reactor.
3. The process according to claim 1 , wherein said catalyst is a MFI zeolite catalyst.
4. The process according to claim 1 , wherein the catalyst is an alkaline earth metal-containing MFI zeolite catalyst, the MFI zeolite having a Si/Al molar ratio of from 10 to 300 and an alkaline earth metal/Al molar ratio of from 0.75 to 15.
5. The process according to claim 2 , wherein the catalyst is an alkaline earth metal-containing MFI zeolite catalyst, the MFI zeolite having a Si/Al molar ratio of from 10 to 300 and an alkaline earth metal/Al molar ratio of from 0.75 to 15.
6. The process according to claim 3 , wherein the catalyst is an alkaline earth metal-containing MFI zeolite catalyst, the MFI zeolite having a Si/Al molar ratio of from 10 to 300 and an alkaline earth metal/Al molar ratio of from 0.75 to 15.