Coating process for ophthalmic lenses
View Patent ↗The present invention generally relates to a method for coating ophthalmic lenses, preferably contact lenses, more preferably silicone hydrogel contact lenses. In particular, the present invention is directed to a method for forming a coating comprising a polyionic material on a contact lens, preferably a silicone hydrogel contact lens, directly in the primary package and maintaining the coated contact lens within said primary package until insertion of the coated contact lens in the eye of the contact lens user.
1. A method for coating an ophthalmic lens in a primary package comprising the steps of:
(a) forming a first polyionic coating solution comprising at least one positively charged polyionic material which is polyamidoamine epichlorohydrin;
(b) forming a second polyionic coating solution comprising at least one negatively charged polyionic material;
(c) forming a coating on an ophthalmic lens by contacting the ophthalmic lens in the primary package with said first polyionic coating solution and adding said second polyionic coating solution to said first polyionic coating solution, wherein the coating comprises said negatively charged material and said positively charged material and the ophthalmic lens with the coating thereon is immersed in a remaining-after-coating solution in the primary package;
(d) sealing the primary package containing the ophthalmic lens immersed in the remaining after-coating solution;
(e) autoclaving and then maintaining said coated ophthalmic lens in said primary package with the remaining after-coating solution until insertion of the ophthalmic lens in the eye of the ophthalmic lens user, wherein the remaining after-coating solution in the primary package is ophthalmically compatible and has an osmolarity from 270 to 350 mOsmol/kg.
2. A method according to claim 1 , wherein step (c) comprises (c10) dispensing said first polyionic coating solution into a primary package; and (c20) placing an ophthalmic lens into said (first) solution in the primary package.
3. A method according to claim 1 , wherein step (c) comprises (c11) placing an ophthalmic lens in the primary package; and (c22) dispensing said first polyionic coating solution into the primary package comprising said ophthalmic lens.
4. A method according to claim 1 , wherein the negatively charged polyionic material comprises a poly acrylic acid (PAA), a carboxymethyl cellulose (CMC) or a poly (styrene sulfonate) (PSS).
5. A method according to claim 1 , wherein said ophthalmic lens is preconditioned by the steps of:
providing a solvent;
allowing the ophthalmic lens to swell in said solvent;
removing the ophthalmic lens from said solvent after swelling; and
transferring said ophthalmic lens to step (c) above.
6. A method according to claim 5 , wherein said solvent comprises an alcohol.
7. A method for coating an ophthalmic lens in a primary package comprising the steps of:
(a) forming a first polyionic coating solution comprising at least one negatively charged polyionic material;
(b) forming a second polyionic coating solution comprising at least one positively charged polyionic material which is polyamidoamine epichlorohydrin;
(c) forming a coating on an ophthalmic lens by contacting the ophthalmic lens in the primary package with said first polyionic coating solution and adding said second polyionic coating solution to said first polyionic coating solution, wherein the coating comprises said negatively charged material and said positively charged material and the ophthalmic lens with the coating thereon is immersed in a remaining-after-coating solution in the primary package;
(d) sealing the primary package containing the ophthalmic lens immersed in the remaining after-coating solution;
(e) autoclaving and then maintaining said coated ophthalmic lens in said primary package with the remaining after-coating solution until insertion of the ophthalmic lens in the eye of the ophthalmic lens user, wherein the remaining after-coating solution in the primary package is ophthalmically compatible and has an osmolarity from 270 to 350 mOsmol/kg.
8. A method according to claim 7 , wherein step (c) comprises (c10) dispensing said first polyionic coating solution into a primary package; and (c20) placing an ophthalmic lens into said (first) solution in the primary package.
9. A method according to claim 7 , wherein step (c) comprises (c11) placing an ophthalmic lens in the primary package; and (c22) dispensing said first polyionic coating solution into the primary package comprising said ophthalmic lens.
10. A method according to claim 7 , wherein the negatively charged polyionic material comprises a poly acrylic acid (PAA), a carboxymethyl cellulose (CMC) or a poly (styrene sulfonate) (PSS).
11. A method according to claim 7 , wherein said ophthalmic lens is preconditioned by the steps of:
providing a solvent;
allowing the ophthalmic lens to swell in said solvent;
removing the ophthalmic lens from said solvent after swelling; and
transferring said ophthalmic lens to step (c) above.
12. A method according to claim 11 , wherein said solvent comprises an alcohol.
13. A method for coating an ophthalmic lens in a primary package comprising the steps of:
(a) forming a first polyionic coating solution, said first polyionic coating solution comprising at least one negatively charged polyionic material and at least one positively charged polyionic material which is polyamidoamine epichlorohydrin, wherein the molar charge ratio of said at least one negatively charged polyionic material and at least one positively charged polyionic material is from 1:100 to 100:1, wherein the first polyionic coating solution has a pH of less than 6.0,
(c) forming a coating on an ophthalmic lens by contacting the ophthalmic lens in the primary package with said first polyionic coating solution wherein the coating comprises said negatively charged material and said positively charged material and the ophthalmic lens with the coating thereon is immersed in a remaining-after-coating solution in the primary package;
(d) sealing the primary package containing the ophthalmic lens immersed in the remaining after-coating solution;
(e) autoclaving and then maintaining said coated ophthalmic lens in said primary package with the remaining after-coating solution until insertion of the ophthalmic lens in the eye of the ophthalmic lens user, wherein the remaining after-coating solution in the primary package is ophthalmically compatible and has an osmolarity from 270 to 350 mOsmol/kg.
14. A method according to claim 13 , wherein the molar charge ratio of said at least one negatively charged polyionic material and at least one positively charged polyionic material is from 1:10 to 10:1.
15. A method according to claim 13 , wherein step (c) comprises (c10) dispensing said first polyionic coating solution into a primary package; and (c20) placing an ophthalmic lens into said (first) solution in the primary package.
16. A method according to claim 13 , wherein step (c) comprises (c11) placing an ophthalmic lens in the primary package; and (c22) dispensing said first polyionic coating solution into the primary package comprising said ophthalmic lens.
17. A method according to claim 13 , wherein the coating on said ophthalmic lens in step (c) is formed without further action.
18. A method according to claim 13 , wherein the negatively charged polyionic material comprises a poly acrylic acid (PAA), a carboxymethyl cellulose (CMC) or a poly (styrene sulfonate) (PSS).
19. A method according to claim 13 , wherein said ophthalmic lens is preconditioned by the steps of:
providing a solvent;
allowing the ophthalmic lens to swell in said solvent;
removing the ophthalmic lens from said solvent after swelling; and
transferring said ophthalmic lens to step (c) above.
20. A method according to claim 19 , wherein said solvent comprises an alcohol.