Manufacturing process of electrodes for electrolysis
View Patent ↗A process for manufacturing electrodes for electrolysis, including steps of forming an arc ion plating (AIP) undercoating layer including valve metal or valve metal alloy containing a crystalline tantalum component and a crystalline titanium component on a surface of the electrode substrate comprising valve metal or valve metal alloy, by an arc ion plating method; heat sintering, including the steps of coating a metal compound solution, which includes valve metal as a chief element, onto the surface of the AIP undercoating layer, followed by heat sintering to transform only the tantalum component of the AIP undercoating layer into an amorphous substance, and to form an oxide interlayer, which includes a valve metal oxides component as a chief element, on the surface of the AIP undercoating layer containing the transformed amorphous tantalum component and the crystalline titanium component; and forming an electrode catalyst layer on the surface of the oxide interlayer.
1. A process for manufacturing electrodes for electrolysis, comprising the steps of:
forming an arc ion plating undercoating layer comprising valve metal comprising a crystalline tantalum component and a crystalline titanium component or valve metal alloy comprising a crystalline tantalum component and a crystalline titanium component on a surface of an electrode substrate comprising valve metal or valve metal alloy, by an arc ion plating method;
heat sintering, comprising
coating a metal compound solution, comprising one or more of titanium, tantalum, niobium, zirconium, hafnium, vanadium, molybdenum, and tungsten, onto a surface of said arc ion plating undercoating layer,
followed by heat sintering
to transform only said tantalum component of said arc ion plating undercoating layer into an amorphous substance, and
to form an oxide interlayer, comprising an oxide of one or more of titanium, tantalum, niobium, zirconium, hafnium, vanadium, molybdenum, and tungsten, on said surface of said arc ion plating undercoating layer containing said transformed amorphous tantalum component and said crystalline titanium component; and
forming an electrode catalyst layer for electrolysis, said electrode catalyst layer comprising one or more of precious metals and precious metal oxides, on a surface of said oxide interlayer.
2. A process for manufacturing electrodes for electrolysis according to claim 1 , wherein a sintering temperature of said heat sintering is 530 degrees Celsius or more, and a sintering duration of said heat sintering is 40 minutes or more.
3. A process for manufacturing electrodes for electrolysis according to claim 1 , wherein
a sintering temperature of said heat sintering is 550 degrees Celsius or more, and a sintering duration of said heat sintering is 60 minutes or more; and
only said tantalum component of said arc ion plating undercoating layer is transformed into said amorphous substance, and said valve metal or valve metal alloy of said arc ion plating undercoating layer is partially transformed into oxides.
4. A process for manufacturing electrodes for electrolysis according to claim 1 , wherein a thermal decomposition process is applied to form said electrode catalyst layer.
5. A process for manufacturing electrodes for electrolysis according to claim 1 , wherein said electrode substrate comprising said valve metal or valve metal alloy is titanium or titanium base alloy.
6. A process for manufacturing electrodes for electrolysis according to claim 1 , wherein said valve metal or valve metal alloy forming said arc ion plating undercoating layer further comprises at least one of niobium, zirconium, and hafnium.