Method for manufacturing wind turbine blade with an integrated lightning conductor
View Patent ↗A method is provided for manufacturing a wind turbine rotor blade in which the blade is formed as a laminated structure by laying a composite material of fiber reinforcement material and/or core material in a mold defining the shape of the blade; evacuating the mold after laying the composite material; introducing a liquid polymer into the evacuated mold and wetting the composite material; curing the liquid polymer after the composite material has been wetted; and removing the mold after curing the liquid. At least one lightning conductor is integrated into the composite material before wetting it with the liquid polymer. Moreover, a wind turbine rotor blade made from a single laminated structure is provided with at least one lightning conductor is integrated into the laminated structure.
1. A method for manufacturing a wind turbine rotor blade in which the blade is formed as a laminated structure, comprising:
laying a composite material of fibre reinforcement material and/or core material in a mould defining the shape of the blade;
integrating a first lightning conductor into the composite material;
evacuating the mould after laying the composite material;
introducing a liquid polymer into the evacuated mould and wetting the composite material;
curing the liquid polymer after the composite material has been wetted; and
removing the mould after curing the liquid polymer,
wherein a first lightning conductor is integrated into the composite material before wetting the composite material, and
wherein the first lightning conductor is braided.
2. The method as claimed in claim 1 , wherein the first lightning conductor is covered by glass fibre.
3. The method as claimed in claim 1 , wherein the braided first lightning conductor is placed along a centre line of the wind turbine blade.
4. The method as claimed in claim 1 , wherein the first lightning conductor is integrated during laying the composite material on an outer mould part and/or a mould core.
5. The method as claimed in claim 1 , wherein an outside lightning receptor is connected to the metallic block after the liquid polymer has cured and the mould has been removed.
6. The method as claimed in claim 1 , wherein the braided conductor is placed next to a shear web of the wind turbine blade.
7. The method as claimed in claim 1 ,
wherein the wind turbine blade comprises a tip and a trailing edge,
wherein a metallic block is placed close to the tip and/or along the trailing edge when laying the composite material, and
wherein the first lightning conductor is connected to the metallic block.
8. The method as claimed in claim 7 ,
wherein the metallic block is located close to the tip,
wherein the wind turbine blade further comprises a second lightning conductor having a first end and a second end, and
wherein the first end is connected to the first lightning conductor the second end is connected to a further metallic block which is placed along the trailing edge.
9. The method as claimed in claim 7 ,
wherein a first portion of the metallic block is located close to the tip and a second portion is located near the trailing edge,
wherein the first lightning conductor is connected to the first portion of the metallic block,
wherein the wind turbine blade further comprises a second lightning conductor having a first end and a second end, and
wherein the first end is connected to the first lightning conductor the second end is connected to the second portion of the metallic block.
10. A method for manufacturing a wind turbine rotor blade in which the blade is formed as a laminated structure, comprising:
laying a composite material of fibre reinforcement material and/or core material in a mould defining the shape of the blade;
integrating a first lightning conductor into the composite material;
evacuating the mould after laying the composite material;
introducing a liquid polymer into the evacuated mould and wetting the composite material;
curing the liquid polymer after the composite material has been wetted; and
removing the mould after curing the liquid polymer,
wherein a first lightning conductor is integrated into the composite material before wetting the composite material, and
wherein the first lightning conductor is integrated during laying the composite material on an outer mould part and/or a mould core.
11. The method as claimed in claim 10 , wherein the first lightning conductor is flat and/or braided.
12. The method as claimed in claim 11 ,
wherein the flat and/or braided conductor is placed next to a shear web of the wind turbine blade.
13. The method as claimed in claim 11 , wherein the flat and/or braided first lightning conductor is placed along a centre line of the wind turbine blade.
14. A method for manufacturing a wind turbine rotor blade in which the blade is formed as a laminated structure, comprising:
laying a composite material of fibre reinforcement material and/or core material in a mould defining the shape of the blade;
integrating a first lightning conductor into the composite material;
evacuating the mould after laying the composite material;
introducing a liquid polymer into the evacuated mould and wetting the composite material;
curing the liquid polymer after the composite material has been wetted; and
removing the mould after the liquid polymer,
wherein a first lightning conductor is integrated into the composite material before wetting the composite material, and
wherein an outside lightning receptor is connected to the metallic block after the liquid polymer has cured and the mould has been removed.