Laminating polyester onto metal substrate

1. Processing steps for laminating a metal substrate with a thin thermoplastic polymer film to create desirable simultaneous commercial properties comprising:

a. uncoiling a metal substrate from a coil on a processing line,

b. wherein said metal substrate is flat rolled,

c. increasing the surface energy of a first major side of said metal substrate to a dyne level of at least 45,

d. preheating said metal substrate to at least 200 degrees F.,

e. preselecting a first film for bonding to said first major side,

f. pressing said first film onto said first major side by use of a first roll,

g. utilizing a first chemical bond for adhering said first film to said first major side thereby creating a metal polymer laminate,

h. wherein said first film comprises at least 50% thermoplastic polyester by weight,

i. wherein said polyester is PET, PBT, or a mixture of PET and PBT,

j. wherein said first film is a maximum of 0.003 inches thick,

k. wherein said first film comprises at least one layer,

l. post treating said metal polymer laminate by heating said metal polymer laminate to at least the lowest melting point of any polymer in said first film, and

m. cooling said metal polymer laminate to below 150 degrees F. for coiling into a finished coil, and

n. wherein said cooling of said metal polymer laminate creates crystallinity in said first film according to a predetermined criterion,

whereby said finished coil has said desirable simultaneous commercial properties comprising:

o. coating continuity of at least three metal thickness bending radius without metal

exposure,

p. bonding of said first film onto said metal substrate of at least 43 ounces per inch after said cooling,

q. a minimum pencil hardness of 2 B.

2. The processing steps according to claim 1 wherein the following steps are optionally done prior to said post treating of said metal polymer laminate:

r. additionally heating said metal polymer laminate to at least 200 degrees F. if necessary,

s. increasing the surface energy of the second major side of said metal substrate to a dyne level of at least 45,

t. preselecting a second film for bonding to the second major side of said metal substrate,

u. pressing said second film onto the second major side by use of a second roll,

v. wherein said second roll is

i. opposite of said first roll to create a roll nip, or

ii. a selected distance sequentially after said first roll,

w. utilizing a second chemical bond for adhering said second film to the second major side,

x. wherein said second film comprises at least one layer, and

y. wherein said second film is a maximum of 0.003 inches thick.

3. The processing steps according to claim 2 wherein any said film is trimmed to substantially match the width of said metal substrate prior to being pressed against said metal substrate.

4. The processing steps according to claim 3 wherein any metal exposure is no more than ⅛ of an inch from the metal substrate edge.

5. The processing steps according to claim 2 wherein any said film is moved to match the position of said metal substrate on said processing line, and the movement speed of any said film is 2 percent or less of the lengthwise speed of said metal substrate on said processing line.

6. The processing steps according to claim 2 wherein the crystallinity of any said polyester is maximized by timing said cooling of polymer metal laminate.

7. The processing steps according to claim 2 wherein any said increasing of said surface energy and preheating of said metal substrate is simultaneously done by a controlled flame.

8. The processing steps according to claim 2 wherein a surface texture roll is applied to either major side of said metal polymer laminate just prior to said cooling.

9. The processing steps according to claim 8 wherein the surface texture alters the gloss of the polymer or creates a desirable commercial texture.

10. The processing steps according to claim 9 wherein said desirable commercial texture includes anti finger print, matte finishes, highly reflective finishes, logos, and embossed patterns.

11. The processing steps according to claim 2 wherein any said chemical bond is created by use of an anhydride, acrylic acid, glycol, or an acrylate molecular group.

12. The processing steps according to claim 2 wherein a terpolymer is utilized as a tie layer for said first film and said terpolymer has both an anhydride functionality and an acrylate functionality.

13. The processing steps according to claim 2 wherein said crystallinity is at least 50% when compared against a highly crystalline form of said polyester.

14. The processing steps according to claim 2 wherein no visible air bubbles are entrapped between any said film and said metal substrate at a size greater than 0.5 microns.

15. The processing steps according to claim 2 wherein at least one of the group comprising i) said first roll and ii) said second roll is heated to a controlled temperature.

16. The processing steps according to claim 2 wherein said processing line includes strip storage to allow coils to be spliced together inline.

17. The processing steps according to claim 2 wherein any said pretreating is automatically regulated based on the lengthwise speed of said metal substrate on said processing line.

18. The processing steps according to claim 2 wherein any said preheating is automatically regulated based on the lengthwise speed of said metal substrate on said processing line and includes any efficiency effects that vary with the lengthwise speed of said metal substrate on said processing line.

19. The processing steps according to claim 2 wherein said post treating is automatically regulated based on the lengthwise speed of said metal substrate on said processing line and includes any efficiency effects that vary with the lengthwise speed of said metal substrate on said processing line.