Process for the production of metal oxide powders
View Patent ↗Process for the production of a metal oxide powder having a BET surface area of at least 20 m 2 /g by reacting an aerosol with oxygen in a reaction space at a reaction temperature of more than 700° C. and then separating the resulting powder from gaseous substances in the reaction space, wherein the aerosol is obtained by atomisation using a multi-component nozzle of at least one starting material, as such in liquid form or in solution, and at least one atomising gas, the volume-related mean drop diameter D 30 of the aerosol is from 30 to 100 μm and the number of aerosol drops larger than 100 μm is up to 10%, based on the total number of drops, and metal oxide powder obtainable by this process.
1. A cerium oxide powder which is in the form of aggregates of primary particles, wherein the aggregates exhibit no cenospherical structure, and the powder has a BET surface area of from 30 to 60 m 2 /g and an isoelectric point at a pH value of from 9 to 11.
2. The cerium oxide powder according to claim 1 , wherein the mean primary particle diameter is from 5 to 30 nm and the mean aggregate diameter is from 20 to 200 nm.
3. The cerium oxide powder according to claim 1 , wherein the proportion of coarse particles >45 μm is less than 100 ppm.
4. The cerium oxide powder according to claim 1 , wherein the content of carbon is less than 0.15 wt.% and the content of chloride, sodium and potassium is less than 300 ppm.
5. A catalyst or catalyst support comprising the cerium oxide powder according to claim 1 .
6. A catalyst or catalyst support comprising the cerium oxide powder according to claim 2 .
7. A catalyst or catalyst support comprising the cerium oxide powder according to claim 3 .
8. A catalyst or catalyst support comprising the cerium oxide powder according to claim 4 .
9. The cerium oxide powder according to claim 1 , wherein the cerium oxide powder is obtained by a process comprising reacting an aerosol with oxygen in a reaction space at a reaction temperature of more than 700° C. and then separating the resulting powder from gaseous substances in the reaction space, wherein the aerosol is obtained by atomising using a multi-component nozzle at least one starting material comprising cerium, in liquid form or in solution, and at least one atomising gas; the volume-related mean drop diameter D 30 of the aerosol is from 30 to 100 μm; and the number of aerosol drops larger than 100 μm is up to 10%, based on the total number of drops.
10. The cerium oxide powder according to claim 9 , wherein the cerium oxide powder is obtained by a process comprising reacting an aerosol with oxygen in a reaction space at a reaction temperature of more than 700° C. and then separating the resulting powder from gaseous substances in the reaction space, wherein the aerosol is obtained by atomising using a multi-component nozzle at least one starting material comprising cerium, in liquid form or in solution, and at least one atomising gas; the volume-related mean drop diameter D 30 of the aerosol is from 30 to 100 μm; and the number of aerosol drops larger than 100 pin is up to 10 %, based on the total number of drops; the multi-component nozzle is a three-component nozzle or four-component nozzle; and two or three separate solutions which comprise the same or different starting materials, in the same or different solvents, in the same or different concentrations, are atomized with the three-component nozzle or four-component nozzle, in addition to the atomising gas.