INDIUM ZINC OXIDE BASED SPUTTERING TARGET, METHOD OF MANUFACTURING THE SAME, AND INDIUM ZINC OXIDE BASED THIN FILM
Disclosed are an indium (In) zinc (Zn) oxide based sputtering target, a method of manufacturing the same, and an In Zn oxide based thin film deposited using the In Zn oxide based sputtering target. The In Zn oxide based sputtering target has a composition of (MO 2 ) x (In 2 O 3 ) y (ZnO) z , in which x:y is about 1:0.01 to 1:1, y:z is about 1:0.1 to 1:10, and M is at least one metal selected from a group consisting of hafnium (Hf), zirconium (Zr), and titanium (Ti).
1 . An indium zinc oxide based sputtering target having a composition of (MO 2 ) x (In 2 O 3 ) y (ZnO) z , wherein x:y is about 1:0.01 to 1:1, y:z is about 1:0.1 to 1:10, and M is at least one metal selected from a group consisting of hafnium (Hf), zirconium (Zr), and titanium (Ti).
2 . The indium zinc oxide based sputtering target of claim 1 , wherein the sputtering target is used in a direct current (DC) sputtering.
3 . The indium zinc oxide based sputtering target of claim 1 , wherein the sputtering target has an electrical resistivity of about 100 mΩ or less.
4 . An indium zinc oxide based thin film which is deposited using the sputtering target of claim 1 in a DC sputtering, wherein an electron mobility is about 1 cm 2 /V·s to 100 cm 2 /V·s.
5 . The indium zinc oxide based thin film of claim 4 , wherein the thin film is deposited under a mixed gas atmosphere of an argon gas and an oxygen gas in which a volume of the oxygen gas is about 0% to 30%.
6 . The indium zinc oxide based thin film of claim 4 , wherein the thin film is amorphous.
7 . The indium zinc oxide based thin film of claim 4 , wherein a surface Root Mean Square (RMS) roughness of the thin film is about 100 Å or less.
8 . A method of manufacturing an indium zinc oxide based sputtering target, the method comprising:
adding, in a slurry in which an indium oxide powder and a zinc oxide powder are added, at least one oxide powder selected from a group consisting of a hafnium oxide, a zirconium oxide, and a titanium oxide to thereby prepare a slurry mixture;
adding a dispersant in the slurry mixture and wet-milling the slurry mixture;
drying the slurry mixture to form a granular powder;
pressing the granular powder to obtain a pressed body; and
sintering the pressed body.
9 . The method of claim 8 , wherein the adding of the at least one oxide powder includes:
mixing and wet-milling a first oxide powder, a first dispersant, and water to prepare a first oxide slurry;
mixing and wet-milling the indium oxide powder, a second dispersant, and water to prepare an indium oxide slurry;
mixing and wet-milling the zinc oxide powder, a third dispersant, and water to prepare a zinc oxide slurry; and
mixing the first oxide slurry, the indium oxide slurry, and the zinc oxide slurry.
10 . The method of claim 9 , wherein at least one of the first dispersant, the second dispersant, and the third dispersant is a polycarbonic acid-ammonium salt or a polyacrylic acid-ammonium salt.
11 . The method of claim 9 , wherein about 0.8 to 2.0 wt % of the first dispersant is contained in the first oxide slurry, about 0.5 to 1.5 wt % of the second dispersant is contained in the indium oxide slurry, and about 0.1 to 0.5 wt % of the third dispersant is contained in the zinc oxide slurry.
12 . The method of claim 8 , wherein the granular powder exhibits an apparent density of about 1.3 or more by American Society for Testing and Materials (ASTM) of an international standards organization.
13 . The method of claim 8 , wherein the sintering is performed at a temperature of about 1,300° C. to 1,500° C. and under an oxygen atmosphere or an air atmosphere.