Method of manufacturing S-glass fibers in a direct melt operation and products formed there from
View Patent ↗A method of forming high strength glass fibers in a refractory-lined glass meter, products made there from and batch compositions suited for use in the method are disclosed. The glass composition for use in the method of the present invention is up to about 64-75 weight percent SiO 2 , 16-24 weight percent Al 2 O 3 , 8-12 weight percent MgO and 0.25-3 weight percent R 2 O, where R 2 O equals the sum of Li 2 O and Na 2 O, has a fiberizing temperature less than about 2650° F., and a ΔT of at least 80° F. By using oxide-based refractory-lined furnaces the cost of production of glass fibers is substantially reduced in comparison with the cost of fibers produced using a platinum-lined melting furnace. High strength composite articles including the high strength glass fibers are also disclosed.
1. A process for producing glass from raw glass-forming material in a refractory-lined glass melter, the glass melter having a roof, a bottom and side walls, defining an elongated channel having a melting zone and a downstream refining zone, the process comprising the steps of:
charging raw glass batch to the melting zone of the refractory-lined glass melter, the glass batch comprising:
68-69 weight percent SiO 2 ;
20-22 weight percent Al 2 O 3 ;
9-10 weight percent MgO;
no more than 2.0 weight percent CaO; and
1-3 weight percent Li 2 O;
providing at least one burner within the roof of the glass melter; and
melting the glass batch to form a fiberizable molten glass, wherein said molten glass produced has a fiberizing temperature of less than about 2650° F.
2. The process of claim 1 , wherein said glass fibers produced have a strength of greater than about 700 KPsi.
3. The process of claim 1 , wherein the glass batch comprises:
less than 5 weight percent total of compounds selected from the group consisting of P 2 O 3 , ZnO, ZrO 2 , SrO, BaO, SO 3 , F2, B 2 O 3 , TiO 2 and Fe 2 O 3 .
4. The process of claim 1 , wherein glass produced from the batch is fiberized at a foiniing temperature of less than 2600° F.
5. The process of claim 1 , wherein said molten glass produced from the batch has a liquidus temperature, wherein the difference (ΔT) between the fiberizing temperature and the liquidus temperature is 140° F.
6. A process for producing glass fibers from raw glass batch in a refractory-lined glass melter, the process comprising the steps of:
charging raw glass batch to the melting zone of a refractory-lined glass melter, the glass batch comprising:
about 68-69 weight percent SiO 2 ;
about 20-22 weight percent Al 2 O 3 ;
about 9-10 weight percent MgO;
no more than 2.0 weight percent CaO; and
about 1-3 weight percent Li 2 O,
heating the glass batch to form a fiberizable molten glass having a fiberizing temperature of less than about 2650° F.; and
fiberizing said molten glass to produce glass fibers having a strength of greater than about 700 KPsi.