Modifier for concrete and cement formulations and methods of preparing the same
View Patent ↗Disclosed are wax emulsion modifiers for concrete and cement formulations and methods for preparing same. The modifiers are applicable to pervious concrete, used in residential areas, parking lots and parks to more effectively manage storm waters and improve environmental practices. This invention also relates to conventional Portland cement concrete mix designs with little to no sand, which provide improved workability, low hydration rates without sacrificing strength while achieving high levels of porosity for water transmission.
1. A method for preparing an aqueous emulsion, for providing a pervious cementitious composition with a field strength of greater than 2000 psi and greater than 20% voids, the method comprising:
combining water, a paraffin hydrocarbon wax, a saponifiable wax, a dispersant, and a saponifier;
heating the combination to a temperature of between about 185° F. (85° C.) to about 205° F. (96.1° C.);
homogenizing the mixture; and then
blending the mixture with at least cement.
2. The method of claim 1 , wherein the mixture is homogenized with cement and aggregate.
3. The method of claim 1 , wherein the aqueous emulsion consists essentially of:
(a) a paraffin hydrocarbon wax,
(b) a saponifiable wax,
(c) a saponifier,
(d) a dispersant, and
(e) water.
4. The method of claim 1 , wherein the cement comprises a mixture of Portland cement and class 1 fly ash.
5. The method of claim 1 , wherein:
the paraffin hydrocarbon wax has a melting point between about 50° C. to about 70° C., and
the saponifiable wax comprises a Montan wax having a melting point in the range of between about 70° C. to about 100° C., an acid number greater than 25, and a saponification number of greater than 85.
6. The method of claim 1 , wherein the saponifier comprises ammonia hydroxide or an alkali metal hydroxide.
7. The method of claim 1 , wherein the dispersant comprises polynaphthalenesulfonic acid in an amount of about 0.1 to about 5 wt % based upon the weight of the emulsion.
8. The method of claim 1 , wherein the Montan wax is present in an amount of about 0.01 to about 10 parts, by weight, per 100 parts of the paraffin hydrocarbon wax.
9. A pervious concrete composition comprising:
an aqueous emulsion comprising:
a paraffin hydrocarbon wax;
a saponifiable wax;
a saponifier; and
a dispersant; and
dry cement; and
aggregate, wherein the pervious concrete composition has a field strength of greater than 2000 psi and greater than 20% voids.
10. The pervious concrete composition of claim 9 wherein the composition is free of high range water reducers, viscosity/rheology modifiers or mix retarders.
11. The pervious concrete composition of claim 9 wherein the composition exhibits an alkalinity comparable to that of a Portland cement concrete mix and wherein the emulsion mixes without separation.
12. The pervious concrete composition of claim 9 , wherein the aqueous emulsion consists essentially of:
(a) a paraffin hydrocarbon wax,
(b) a saponifiable wax,
(c) a saponifier,
(d) a dispersant, and
(e) water.
13. The pervious concrete composition of claim 12 , wherein the aqueous emulsion consists essentially of:
about 38.68 wt % of paraffin wax;
about 1 wt % on Montan wax;
about 1 wt % of polynapthalenesulfonic acid dispersant;
about 0.25 wt % of 45% aqueous potassium hydroxide; and
about 59.07 wt % water.
14. The pervious concrete composition of claim 9 , wherein the dry cement comprises a mixture of Portland cement and class 1 fly ash.
15. The pervious concrete composition of claim 9 , wherein:
the paraffin hydrocarbon wax has a melting point between about 50° C. to about 70° C., and
the saponifiable wax comprises a Montan wax having a melting point in the range of between about 70° C. to about 100° C., an acid number greater than 25, and a saponification number of greater than 85.
16. The pervious concrete composition of claim 9 , wherein the saponifier comprises ammonia hydroxide or an alkali metal hydroxide.
17. The pervious concrete composition of claim 9 , wherein the dispersant comprises polynaphthalenesulfonic acid in an amount of about 0.1 to about 5 wt % based upon the weight of the emulsion.
18. The pervious concrete composition of claim 9 , wherein the Montan wax is present in an amount of about 0.01 to about 10 parts, by weight, per 100 parts of the paraffin hydrocarbon wax.