Expandable functional TFE copolymer fine powder, the expandable functional products obtained therefrom and reaction of the expanded products
View Patent ↗A functional TFE copolymer fine powder is described, wherein the TFE copolymer is a polymer of TFE and at least one functional comonomer, and wherein the TFE copolymer has functional groups that are pendant to the polymer chain. The functional TFE copolymer fine powder resin is paste extrudable and expandable. Methods for making the functional TFE copolymer are also described. The expanded functional TFE copolymer material may be post-reacted after expansion.
1. A functional tetrafluoroethylene (TFE) copolymer fine powder resin comprising:
a functional TFE core-shell copolymer comprising:
a core comprising a polymer chain of TFE monomers and at least one comonomer having a functional group pendant to the polymer chain; and
a shell consisting of TFE monomers,
wherein the at least one comonomer having a functional group is present in the copolymer in an amount between 0.01 mol % and 5 mol % of the functional TFE core-shell copolymer,
wherein the at least one comonomer having a functional group is a fluorovinyl ether of the general formula CF 2 ═CF—OR f Z, where R f represents a fluoroalkylene group optionally interrupted by one or more oxygen(s) and Z represents a functional group, and
wherein Z is, nitrile, aldehyde, carboxylic acid or salt, ester, amine, amide, carbonyl halide, sulfonyl halide, sulfonic acid or salts thereof, sulfonamide, sulfonimide, anhydride, sulfide, phosphonic acid or salts thereof, hydroxy (alcohol) sulfate esters, phosphate esters, or isocyanate.
2. The functional TFE copolymer fine powder resin of claim 1 , wherein the at least one comonomer having a functional group present in the copolymer is between 0.01 and 3 mol % the functional TFE core-shell copolymer.
3. The functional TFE copolymer fine powder resin of claim 1 , wherein the at least one comonomer having a functional group present in the copolymer is between 0.01 and 2 mol % of the functional TFE core-shell copolymer.
4. The functional TFE copolymer fine powder resin of claim 1 , wherein the fluorovinyl ether is selected from ester vinyl ether, sulfonyl fluoride vinyl ether or cyano vinyl ether.
5. The functional TFE copolymer fine powder resin of claim 1 , wherein the at least one comonomer having a functional group is selected from perfluoro(8-cyano-5-methyl-3,6-dioxa-1-octene) (8 CNVE), perfluoro(8-carboxymethyl-5-methyl-3,6-dioxa-1-octene) (EVE), or perfluoro(8-sulfonic acid fluoride-5-methyl-3,6-dioxa-1-octene) (PSVE).
6. The functional TFE copolymer fine powder resin of claim 1 , wherein said functional TFE core-shell copolymer further comprises a second comonomer comprising a second functional group.
7. The functional TFE copolymer of claim 6 , wherein the second functional group is different from the first functional group.
8. The functional TFE copolymer of claim 6 , wherein the second functional group is the same as the first functional group.
9. The functional TFE copolymer fine powder resin of claim 1 , wherein said functional TFE core-shell copolymer further comprises at least one additional comonomer without a pendant functional group.
10. The functional TFE copolymer fine powder resin of claim 1 , wherein said shell is formed during the last 10-20% of polymerization of said copolymer.
11. The functional TFE copolymer fine powder resin of claim 1 , wherein said shell is formed during the last 10% of polymerization of said copolymer.