Methods for preparing polyurethanes
The present invention provides methods for preparing polyurethanes from reaction components including: (a) reacting about 1 equivalent of at least one polyisocyanate; and about 0.1 to about 0.5 equivalents of at least one polyol having 2 to 18 carbon atoms to form an isocyanate functional urethane prepolymer; and (b) reacting the isocyanate functional urethane prepolymer, about 0.05 to about 1.0 equivalents of at least one branched polyol having 4 to 18 carbon atoms and at least 3 hydroxyl groups; and up to about 0.9 equivalents of at least one polyol different from the branched polyol and having 2 to 18 carbon atoms, wherein the reaction components are essentially free of polyester polyol and polyether polyol, as well as methods for preparing polyurethanes using a one pot process.
1. A method for preparing a polyurethane from reaction components comprising:
(a) reacting about 1 equivalent of at least one polyisocyanate and about 0.3 to about 0.4 equivalents of butanediol or cyclohexane dimethanol to form an isocyanate functional urethane prepolymer; and
(b) reacting the isocyanate functional urethane prepolymer, about 0.1 to about 0.3 equivalents of trimethylolpropane, about 0.4 to about 0.5 equivalents of butanediol or cyclohexane dimethanol; and about 0.01 to about 0.3 equivalents of at least one polycarbonate diol, wherein the reaction product components are essentially free of polyether polyol.
2. The method according to claim 1 , wherein the polyisocyanate and butanediol or cyclohexane dimethanol are each preheated to a temperature of at least about 100° C. prior to reaction.
3. The method according to claim 1 , wherein the isocyanate functional urethane prepolymer, trimethylolpropane, butanediol or cyclohexane dimethanol and the polycarbonate diol are each preheated to a temperature of at least about 100° C. prior to reaction.
4. The method according to claim 1 , wherein the reaction components are maintained at a temperature of at least about 100° C. for at least about 10 minutes.
5. The method according to claim 4 , wherein the reaction components are maintained at a temperature of at least about 110° C. for at least about 10 minutes.
6. The method according to claim 5 , wherein the reaction components are maintained at a temperature of at least about 120° C. for at least about 10 minutes.
7. The method according to claim 1 , wherein the reaction components are mixed in a mixing chamber for at least about 4 seconds prior to forming an article.
8. The method according to claim 1 , wherein the polyurethane is cured at a temperature of at least about 100° C. for at least about 2 hours.