Silica encapsulated organic nanopigments and method of making same
View Patent ↗Core-shell nanoscale pigment particles include a core organic pigment composition including nanoscale particles of organic pigments, and a shell layer of surface-deposited silica, where the organic pigment particles are selected from azo-type pigment particles, azo laked pigment particles, quinacridone pigment particles, phthalocyanine pigment particles, and mixtures thereof. The core-shell nanoscale pigment particles can also include an organic primer layer covering the core and located between the core and the shell layer. The core-shell nanoscale pigment particles can be made by preparing a core composition including nanoparticles of organic pigments, and encapsulating the core with shell layer of surface-deposited silica and an optional organic primer layer located between the core and the shell layer.
1. Core-shell nanoscale pigment particles, comprising:
a core comprised of nanoscale particles of organic pigments having a surface-associated sterically bulky stabilizer, the organic pigments having at least one functional moiety, the surface-associated sterically bulky stabilizer having at least one functional group, and wherein the functional moiety of the organic pigments associates non-covalently with the at least one functional group of the stabilizer, and
a shell layer comprised of surface-deposited silica that encapsulates the core,
wherein:
the organic pigment particles are selected from the group consisting of azo-type pigment particles, azo laked pigment particles, quinacridone pigment particles, phthalocyanine pigment particles, and mixtures thereof.
2. The core-shell nanoscale pigment particle of claim 1 , wherein the organic pigment is an organic monoazo laked pigment and the at least one functional moiety is selected from the group consisting of sulfonate/sulfonic acid, (thio)carboxylate/(thio)carboxylic acid, phosphonate/phosphonic acid, ammonium and substituted ammonium salts, phosphonium and substituted phosphonium salts, substituted carbonium salts, substituted arylium salts, alkyl/aryl (thio)carboxylate esters, thiol esters, primary or secondary amides, primary or secondary amines, hydroxyl, ketone, aldehyde, oxime, hydroxylamino, enamines (or Schiff base), porphyrins, (phthalo)cyanines, urethane or carbamate, substituted ureas, guanidines and guanidinium salts, pyridine and pyridinium salts, imidazolium and (benz)imidazolium salts, (benz)imidazolones, pyrrolo, pyrimidine and pyrimidinium salts, pyridinone, piperidine and piperidinium salts, piperazine and piperazinium salts, triazolo, tetraazolo, oxazole, oxazolines and oxazolinium salts, indoles, and indenones.
3. The core-shell nanoscale pigment particle of claim 1 , wherein the at least one functional group of the sterically bulky stabilizer is selected from the group consisting of sulfonate/sulfonic acid, (thio)carboxylate/(thio)carboxylic acid, phosphonate/phosphonic acid, ammonium and substituted ammonium salts, phosphonium and substituted phosphonium salts, substituted carbonium salts, substituted arylium salts, alkyl/aryl (thio)carboxylate esters, thiol esters, primary or secondary amides, primary or secondary amines, hydroxyl, ketone, aldehyde, oxime, hydroxylamino, enamines (or Schiff base), porphyrins, (phthalo)cyanines, urethane or carbamate, substituted ureas, guanidines and guanidinium salts, pyridine and pyridinium salts, imidazolium and (benz)imidazolium salts, (benz)imidazolones, pyrrolo, pyrimidine and pyrimidinium salts, pyridinone, piperidine and piperidinium salts, piperazine and piperazinium salts, triazolo, tetraazolo, oxazole, oxazolines and oxazolinium salts, indoles, and indenones.
4. The core-shell nanoscale pigment particle of claim 1 , wherein the sterically bulky stabilizer comprises at least one aliphatic hydrocarbon moiety.
5. The core-shell nanoscale pigment particle of claim 1 , wherein the sterically bulky stabilizer is selected from the group consisting of the following compounds:
wherein Z is H, a metal cation, or an organic cation;
wherein Z is H, a metal cation, or an organic cation, and m+n>1;
wherein Z is H, a metal cation, or an organic cation, and m+n>1 per branch;
wherein Z is H, a metal cation, or an organic cation, and m≧1;
wherein Z is H, a metal cation, or an organic cation, and m≧1; and
wherein Z is H, a metal cation, or an organic cation, and n≦1.
6. The core-shell nanoscale pigment particle of claim 1 , wherein said organic pigment core comprises azo-type or monoazo laked pigment particles.
7. The core-shell nanoscale pigment particle of claim 1 , wherein said organic pigment core comprises quinacridone pigment particles.
8. The core-shell nanoscale pigment particle of claim 1 , wherein said organic pigment core comprises phthalocyanine pigment particles.
9. The core-shell nanoscale pigment particle of claim 1 , wherein said silica shell has a thickness of less than about 50 nm.
10. The core-shell nanoscale pigment particle of claim 1 , wherein said silica shell is prepared by a sol-gel process.
11. The core-shell nanoscale pigment particle of claim 1 , wherein said silica shell comprises hydrophilic, non-functionalized silica.
12. The core-shell nanoscale pigment particle of claim 1 , wherein said silica shell is functionalized with alkyl groups containing 2 or more carbons.
13. The core-shell nanoscale pigment particle of claim 1 , having an average particle size, d 50 , of from about 10 nm to about 250 nm, a particle size distribution having a geometric standard deviation of from about 1.1 to about 1.9, and an aspect ratio of from 1:1 to about 10:1.
14. A process for preparing core-shell nanoscale pigment particles, comprising:
preparing a core comprising nanoparticles of organic pigments having a surface associated sterically bulky stabilizer, the organic pigments having at least one functional moiety, the surface-associated sterically bulky stabilizer having at least one functional group, and wherein the functional moiety of the organic pigments associates non-covalently with the at least one functional group of the stabilizer, and
encapsulating the core with a shell layer comprised of surface-deposited silica,
wherein:
said organic pigment particles are selected from the group consisting of azo-type pigment particles, azo laked pigment particles, quinacridone pigment particles, phthalocyanine pigment particles, and mixtures thereof.
15. The process of claim 14 , wherein said silica shell has a thickness of less than about 50 nm.
16. The process of claim 14 , wherein said silica shell is prepared by a sol-gel process.
17. The process of claim 14 , wherein said silica shell comprises hydrophilic, non-functionalized silica.
18. The process of claim 14 , wherein said silica shell is functionalized with alkyl groups.
19. The process of claim 14 , wherein the preparing of the core comprises:
providing an organic pigment or pigment precursor having the at least one functional moiety,
providing a sterically bulky stabilizer compound having the at least one functional group,
carrying out a chemical reaction, whereby the at least one functional moiety found on the pigment or pigment precursor is non-covalently associated with the at least one functional group of the stabilizer, so as to form the core.
20. The process of claim 14 , wherein said encapsulating comprises a sol-gel polymerization comprising hydrolyzing a silica precursor agent in the presence of an alcohol solvent and optionally water, followed by condensation polymerization.
21. The process of claim 20 , wherein the sol-gel polymerization is a pH-mediated polycondensation in the presence of an acid or base catalyst.
22. An ink composition comprising:
a carrier, and
a colorant comprising core-shell nanoscale pigment particles according to claim 1 .
23. The ink composition of claim 22 , wherein the ink composition is selected from the group consisting of solid ink compositions, phase change ink compositions, curable ink compositions, aqueous ink compositions, and non-aqueous ink compositions.
24. A toner composition comprising:
the core-shell nanoscale pigment particles of claim 1 ,
polymer particles, and
optionally one or more additives.
25. The core-shell nanoscale pigment particle of claim 1 , wherein the surface-deposited silica is obtained from an alkoxysilane precursor reagent, wherein a molar ratio of alkoxysilane:pigment is from about 1:1 to about 10:1.