Polyoxymethylene molding materials and moldings and the use thereof

1. A molding material containing

a) a polyoxymethylene homo- or copolymer having at least 70%, based on the total number of terminal groups, of terminal hydroxyalkylene groups, wherein the polyoxymethylene has been polymerized in the presence of a molecular weight regulator and wherein unstable chain ends of the polyoxymethylene have been degraded by hydrolysis, the polyoxymethylene having a melt volume rate MVR of less than 20 cm 3 /10 minutes, measured according to ISO 1133 at 190° C. and 2.16 kg, and wherein the proportion of component a) of low molecular weight polymers having molecular weights below 10 000 dalton is less than 15% by weight, based on the total mass of the polyoxymethylene, the polyoxymethylene being present in the molding material an amount of from 30% to 95% by weight;

b) a thermoplastic elastomer that has active hydrogen atoms; and at least one component

c) which contains groups for covalent coupling of the components a) and b).

2. The molding material as claimed in claim 1 , wherein the polyoxymethylene has a melt volume rate MVR of less than 10 cm 3 /10 minutes.

3. The molding material as claimed in claim 1 , wherein the proportion of the thermoplastic elastomer is from 15 to 50% by weight, based on the molding material.

4. The molding material as claimed in claim 1 , wherein the proportion of the polyoxymethylene having a molecular weight below 10 000 dalton is from 0 to 5% by weight, based on the total mass of the polyoxymethylene.

5. The molding material as claimed in claim 1 , wherein component c) is a diisocyanate.

6. The molding material as claimed in claim 1 , wherein component b) is a thermoplastic polyester elastomer (TPE-E), a thermoplastic polyamide elastomer (TPE-A) and/or a thermoplastic polyurethane elastomer (TPE-U).

7. The molding material as claimed in claim 5 , which additionally contains, as component d) an oxymethylene homopolymer and/or oxymethylene copolymer differing from component a).

8. The molding material as claimed in claim 7 , which additionally contains stabilizers and processing auxiliaries as component e).

9. The molding material as claimed in claim 8 , wherein the amount of component a) is from 30 to 95% by weight, the amount of component b) is from 5 to 50% by weight, the amount of component c) is up to 10% by weight, the amount of component d) is from 0 to 65% by weight and the amount of component e) is from 0 to 10% by weight, the stated amounts being based on the sum of the components a), b), c), d) and e).

10. A shaped article comprising the molding material as claimed in claim 1 .

11. The shaped article of claim 10 , wherein the shaped article comprises a clip for fixing cable harnesses, a fixing holder, a loudspeaker grill, or a belt release button.

12. The shaped article of claim 10 , wherein the shaped article comprises an antenna socket or a windscreen wiper cap.

13. A molding material as defined in claim 1 , wherein the polyoxymethylene has a melt volume rate MVR of from 0.5 cm 3 /10 minutes to 5 cm 3 /10 minutes.

14. A molding material as defined in claim 1 , wherein the polyoxymethylene has a melt volume rate MVR of from 0.5 cm 3 /10 minutes to 5 cm 3 /10 minutes.

15. A molding material as defined in claim 1 , wherein the molding material has a Charpy notched impact strength of from 29 kJ/m 2 to 140 kJ/m 2 .

16. A molding material as defined in claim 1 , wherein the molding material has a Charpy notched impact strength of greater than 100 kJ/m 2 .

17. A molding material as defined in claim 1 , wherein the molding material has a Charpy notched impact strength of from 50 kJ/m 2 to 140 kJ/m 2 .

18. A molding material as defined in claim 1 , wherein the molding material has a Charpy notched impact strength of from 71 kJ/m 2 to 140 kJ/m 2 .