Process for producing electrolyte material for polymer electrolyte fuel cells, and membrane-electrode assembly for polymer electrolyte fuel cells
View Patent ↗A membrane-electrode assembly for polymer electrolyte fuel cells which is excellent in water repellency and gas diffusivity and which exhibits a high output power density, can be obtained by using, as an electrolyte material for polymer electrolyte fuel cells, a fluoropolymer obtained by contacting a fluoropolymer which is excellent in gas diffusivity and which has alicyclic structures in its main chain and further has sulfonic acid groups, with fluorine gas for fluorination to increase water repellency and stabilize the molecule ends. The above fluoropolymer is preferably made of a copolymer comprising repeating units based on the following monomer A and repeating units based on the following monomer B (wherein Y is a fluorine atom or a trifluoromethyl group, m is an integer of from 0 to 3, p is 0 or 1, and n is an integer of from 1 to 12): Monomer A: A perfluoromonomer which gives a polymer having repeating units containing cyclic structures in its main chain by radical polymerization Monomer B: CF 2 ═CF—(OCF 2 CFY) m -0 p -(CF 2 ) n —SO 3 H.
1. A process for producing a liquid composition which comprises, in order,
(1) obtaining a perfluoropolymer having alicyclic structures in its main chain and further having —SO 2 F groups by radical polymerization;
(2) contacting the perfluoropolymer with fluorine gas;
(3) converting the —SO 2 F groups to sulfonic acid groups, wherein a perfluoropolymer having alicyclic structures in its main chain and further having sulfonic acid groups is produced; and
(4) dissolving or dispersing the perfluoropolymer in a —OH group-containing organic solvent.
2. The process for according to claim 1 , wherein the perfluoropolymer having sulfonic acid groups is made of a copolymer comprising repeating units based on the following monomer A and repeating units based on the following monomer B (wherein Y is a fluorine atom or a trifluoromethyl group, m is an integer of from 0 to 3, p is 0 or 1, and n is an integer of from 1 to 12):
Monomer A: A perfluoromonomer which gives a polymer having repeating units containing cyclic structures in its main chain by radical polymerization
Monomer B: CF 2 ═CF—(OCF 2 CFY) m —O p —(CF 2 ) n —SO 3 H.
3. The process according to claim 2 , wherein the monomer A is selected from the group consisting of perfluoro(3-butenyl vinyl ether), perfluoro(2,2-dimethyl-1,3-dioxole), perfluoro(1,3-dioxole), 2,2,4-trifluoro-5-trifluoromethoxy-1,3-dioxole and perfluoro(2-methylene-4-methyl-1,3-dioxolane), and the monomer B is perfluoro(3,6-dioxa-4-methyl-7-octene)sulfonic acid or perfluoro(3-oxa-4-pentene)sulfonic acid.
4. The process according to claim 3 , wherein the monomer A is selected from the group consisting of perfluoro(2,2-dimethyl-1,3-dioxole), perfluoro(3-butenyl vinyl ether) and perfluoro(2-methylene-4-methyl-1,3-dioxolane), and the monomer B is perfluoro(3,6-dioxa-4-methyl-7-octene)sulfonic acid.
5. The process according to claim 1 , wherein said contacting the perfluoropolymer with fluorine gas is carried out at a temperature of from 150 to 200° C.
6. The process according to claim 1 , wherein said contacting the perfluoropolymer with fluorine gas is carried out over a period of time of from 1 to 50 hours.
7. The process according to claim 1 , wherein said contacting the perfluoropolymer with fluorine gas is carried out over a period of time of from 1 to 50 hours at a temperature of from 150 to 200° C.
8. The process according to claim 1 , wherein the perfluoropolymer is subjected to heat treatment prior to contacting the perfluoropolymer with fluorine gas.
9. The process according to claim 1 , wherein the perfluoropolymer is dispersed or dissolved in a fluorosolvent having no hydrogen atoms prior to contacting the perfluoropolymer with fluorine gas.