Hotmelt process for producing a chemically crosslinked polyurethane film
View Patent ↗Process for producing a chemically crosslinked polyurethane film, comprising the steps of: A) chemically reacting a mixture comprising two or more polyols with one or more polyisocyanates, at least one of the polyols or at least one of the polyisocyanates comprising molecules having a functionality of three or more, to form hydroxyl-functionalized polyurethane hotmelt prepolymer, B) reacting the hydroxyl-functionalized polyurethane hotmelt prepolymer with one or more polyisocyanates in a continuously operating mixing assembly, C) coating the melt emerging from the mixing assembly onto an incoming web-form material or between two incoming web-form materials, in the course of which the reaction started in step B) continues.
1. Process for producing a chemically crosslinked polyurethane film, comprising the steps of
A) chemically reacting a mixture comprising two or more polyols with one or more polyisocyanates, at least one of the polyols or at least one of the polyisocyanates comprising molecules having a functionality of three or more, the ratio of the total number of isocyanate groups to the total number of hydroxyl groups being less than 1.0, to give a hydroxyl-functionalized, meltable reaction product, in the form of a hydroxyl-functionalized polyurethane hotmelt prepolymer,
B) introducing the hydroxyl-functionalized polyurethane hotmelt prepolymer and one or more polyisocyanates into a continuously operating mixing assembly wherein a chemical reaction takes place between the hydroxyl-functionalized polyurethane hotmelt prepolymer and the polyisocyanates in the melt,
C) coating the melt emerging from the mixing assembly onto an incoming web-form material or between two incoming web-form materials, in the course of which the reaction between the hydroxyl-functionalized polyurethane hotmelt prepolymer and the polyisocyanates started in step B) continues to form a chemically crosslinked nonmeltable polyurethane film.
2. Process for producing a chemically crosslinked polyurethane film according to claim 1 , wherein the hydroxyl-functionalized polyurethane hotmelt prepolymer meltable reaction product of step A) is branched.
3. Process for producing a chemically crosslinked polyurethane film according to claim 1 , wherein the ratio of the total number of isocyanate groups to the total number of hydroxyl groups in the polyisocyanates and polyols involved in the chemical reaction to give the hydroxyl-functionalized polyurethane hotmelt prepolymer is between greater than 0.90 and less than 0.98.
4. Process for producing a chemically crosslinked polyurethane film according to claim 1 , wherein the numerical fraction of the molecules having a functionality of three or more that are involved in the chemical reaction to give the hydroxyl-functionalized polyurethane hotmelt prepolymer is at least 0.5%.
5. Process for producing a chemically crosslinked polyurethane film according to claim 1 , wherein the numerical fraction of the molecules involved in the chemical reaction to give the hydroxyl-functionalized polyurethane hotmelt prepolymer that have a relative molar mass of less than or equal to 1000 is at least 70%.
6. Process for producing a chemically crosslinked polyurethane film according to claim 1 , wherein a weight fraction of greater than 70% by weight, based on the polyol fraction, of the polyols involved in the chemical reaction to give the hydroxyl-functionalized polyurethane hotmelt prepolymer are polyether polyols.
7. Process for producing a chemically crosslinked polyurethane film according to claim 1 wherein, in addition to the polyols there are also other isocyanate-reactive compounds involved in the chemical reaction to give the hydroxyl-functionalized polyurethane hotmelt prepolymer.
8. Process for producing a chemically crosslinked polyurethane film according to claim 1 , wherein at least one of the polyisocyanates involved in the chemical reaction to give the hydroxyl-functionalized polyurethane hotmelt prepolymer has a functionality of two or greater than two.
9. Process for producing a chemically crosslinked polyurethane film according to claim 1 , wherein a weight fraction of greater than 70% by weight, based on the polyisocyanate fraction, of the polyisocyanates involved in the chemical reaction to give the hydroxyl-functionalized polyurethane hotmelt prepolymer are aliphatic or cycloaliphatic polyisocyanates.
10. Process for producing a chemically crosslinked polyurethane film according to claim 1 , wherein a weight fraction of greater than 70% by weight, based on the polyisocyanate fraction, of the polyisocyanates involved in the chemical reaction to give the hydroxyl-functionalized polyurethane hotmelt prepolymer comprise isophorone diisocyanate.
11. Process for producing a chemically crosslinked polyurethane film according to claim 1 , wherein the chemical reaction to give the hydroxyl-functionalized polyurethane hotmelt prepolymer takes place with addition of a catalyst.
12. Process for producing a chemically crosslinked polyurethane film according to claim 1 , wherein the chemical reaction to give the hydroxyl-functionalized polyurethane hotmelt prepolymer takes place with addition of a catalyst comprising bismuth and carbon.
13. Process for producing a chemically crosslinked polyurethane film according to claim 1 , wherein the hydroxyl-functionalized polyurethane hotmelt prepolymer comprises fillers, resins, auxiliaries and additives.
14. Process for producing a chemically crosslinked polyurethane film according to claim 1 , wherein the ratio of the total number of isocyanate groups to the total number of hydroxyl groups during the chemical reaction of the hydroxyl-functionalized polyurethane hotmelt prepolymer with the polyisocyanates in the melt in a continuously operating mixing assembly is between greater than 0.90 and less than 1.2.
15. Process for producing a chemically crosslinked polyurethane film according to claim 1 , wherein the chemical reaction of the hydroxyl-functionalized polyurethane hotmelt prepolymer in the melt with one or more polyisocyanates takes place continuously in an extruder.
16. Process for producing a chemically crosslinked polyurethane film according to claim 1 , wherein the chemical reaction of the hydroxyl-functionalized polyurethane hotmelt prepolymer in the melt with one or more polyisocyanates takes place continuously in a two-component mixing and metering unit.
17. Process for producing a chemically crosslinked polyurethane film according to claim 1 , wherein the complex viscosity of the hydroxyl-functionalized polyurethane hotmelt prepolymer, measured at 10 rad/second and 23° C., is greater than 8000 Pas.
18. Process for producing a chemically crosslinked polyurethane film according to claim 1 , wherein the complex viscosity of the hydroxyl-functionalized polyurethane hotmelt prepolymer, measured at 10 rad/second and 70° C., is greater than 300 Pas.
19. Process for producing a chemically crosslinked polyurethane film according to claim 1 , wherein the crosslinked polyurethane film has a thickness of between 20 μm and 3000 μm.
20. Process for producing a chemically crosslinked polyurethane film according to claim 1 , wherein the production takes place solventlessly.
21. Process for producing a chemically crosslinked polyurethane film according to claim 1 , wherein the chemical reaction to give the hydroxyl-functionalized polyurethane hotmelt prepolymer in accordance with step A) takes place continuously.
22. A carrier layer in an adhesive tape or in a self-adhesive article comprising a chemically crosslinked polyurethane film obtained by the process of claim 1 .
23. A pressure-sensitive adhesive layer in an adhesive tape or in a self-adhesive article comprising a chemically crosslinked polyurethane film obtained by the process of claim 1 .
24. A functional layer in an adhesive tape or in a self-adhesive article comprising a chemically crosslinked polyurethane film obtained by the process of claim 1 .
25. Process of claim 12 , wherein said catalyst is a bismuth carboxylate or a bismuth carboxylate derivative.