Acrylic acid and water-absorbing polymer structures based on renewable raw materials and process for their production by dehydration
View Patent ↗The present invention relates to a process for production of acrylic acid, comprising the steps of a) dehydration of glycerine to an acrolein-comprising dehydration product; b) gas phase oxidation of the dehydration product to obtain an acrylic acid-comprising monomer gas; c) bringing into contact of the monomer gas with a quench agent to obtain an acrylic acid-comprising quench phase; and d) work-up of the quench phase to obtain an acrylic acid-comprising monomer phase; whereby, during the dehydration a liquid phase a1 and a gas phase a2 is present, whereby in the liquid phase a1 a plurality of gas bubbles is generated, as well as a process for production of polymers by polymerization of acrylic acid, preferably for production of water-absorbing polymers, the water-absorbing polymers obtainable by this process, a composite, a process for production of a composite, the composite obtainable by this process, and further chemical products.
1. A process for preparation of a polymer by polymerization of acrylic acid, comprising the following steps:
A heating an aqueous glycerine solution before entry into a dehydration reactor to a temperature of from about 250° C. to 310° C. to form glycerine;
B transporting the glycerine of step A to the dehydration reactor;
C dehydrating the glycerine of step B to an acrolein-comprising dehydration product wherein the dehydrating occurs along a path wherein the glycerine concentration decreases, wherein along this path a pressure change occurs, and different flow rates exist;
D gas phase oxidating of the acrolein-comprising dehydration product to obtain an acrylic acid-comprising monomer gas;
E bringing into contact of the monomer gas with a quench agent to obtain an acrylic acid-comprising quench phase;
F working-up the quench phase to obtain an acrylic acid-comprising monomer phase; and
G polymerizing the acrylic acid-comprising monomer phase;
wherein during the dehydration a liquid phase a1 and a gas phase a2 is present, wherein in the liquid phase a1, a plurality of gas bubbles is generated wherein the dehydration occurs at least partially in the liquid phase.
2. The process according to claim 1 , wherein the polymer is a water-absorbing polymer structure.
3. The process according to claim 1 wherein the acrylic acid is present to at least about 20 mol %, based on the monomer, as a salt.
4. The process according to claim 1 wherein at least a part of the plurality of gas bubbles within the liquid phase a1 is conducted.
5. The process according to claim 1 wherein at least a part of the plurality of gas bubbles within the liquid phase a1 is divided.
6. The process according to claim 1 wherein the glycerine is obtained by saponification of fats.
7. The process according to claim 1 wherein the glycerine is produced in the generation of liquid carburants from natural raw materials.
8. The process according to claim 1 wherein the dehydration occurs at a temperature in a range from 100° C. to 400° C.
9. The process according to claim 1 wherein the dehydration occurs at a pressure in a range from 2 to 200 bar.
10. The process according to claim 1 wherein the dehydration occurs with an average reactor residence time in a range from 1 to 30 minutes.
11. The process according to claim 1 wherein the acrolein arising from the dehydration is transferred by the plurality of gas bubble out of the liquid phase a1 into the gas phase a2.
12. The process according to claim 1 wherein the glycerine is warmed to from 270° C. to 290° C.