Foam and Process for Producing the Same
It is intended to provide a resin foam which can be preferably used for medical use, and a flexible silicone type resin foam having a water-absorbing property. The resin foam which has a low toxicity and excellent physical properties for medical use such as moisture permeability, skin compatibility and low irritation can be obtained by using a resin which has a siloxane unit and an oxyalkylene unit in its molecular structure and does not contain a unit derived from an isocyanate group. Further, the flexible silicone type resin foam having a water-absorbing property can be obtained by allowing it to have a specific resin composition and a foam structure.
1 . A resin foam for medical use, comprising resin containing a siloxane unit and an oxyalkylene unit in its molecular structure and containing no isocyanate derived unit.
2 . The resin foam for medical use according to claim 1 , wherein a water absorption represented by equation (1) when immersed in a physiological sodium chloride solution at 37° C. for 24 hours is 200 wt % or more and lower than 2000 wt %:
Water absorption=100×(Foam weight after immersion−Foam weight before immersion)/(Foam weight before immersion) (1).
3 . A flexible water absorbing resin foam, comprising resin containing a siloxane unit and an oxyalkylene unit in its molecular structure and containing no isocyanate derived unit; and having a water absorption represented by equation (1) when immersed in a physiological sodium chloride solution at 37° C. for 24 hours of 200 wt % or more and lower than 2000 wt %:
Water absorption=100×(Foam weight after immersion−Foam weight before immersion)/(Foam weight before immersion) (1).
4 . The resin foam according to claim 1 , wherein the resin comprises an oxyethylene unit as at least one kind of the oxyalkylene unit.
5 . The resin foam according to claim 1 , wherein the resin comprises the oxyethylene unit in a proportion of 5 wt % or more and lower than 80 wt %.
6 . The resin foam according to claim 1 , wherein the resin is obtained by curing a mixture containing:
an alkenyl group-containing compound (A);
a hydrosilyl group-containing compound (B); and
a hydrosilylation catalyst (C).
7 . The resin foam according to claim 6 , wherein the alkenyl group-containing compound (A) is an organic compound containing no siloxane unit in its molecular structure.
8 . The resin foam according to claim 6 , wherein the alkenyl group-containing compound (A) comprises 50 wt % or more of a polyoxyalkylene polymer containing at least one alkenyl group at a terminal.
9 . The resin foam according to claim 6 , which is obtained by further blending a foaming agent (D) in the resin, and then foaming the mixture simultaneously with curing.
10 . The resin foam according to claim 9 , wherein at least one kind of the foaming agent (D) is an active hydrogen group-containing compound.
11 . The resin foam according to claim 10 , wherein the active hydrogen group-containing compound is a compound having an OH group.
12 . The resin foam according to claim 11 , wherein the compound having an OH group is at least one member selected from the group consisting of water, alcohol, and polyether polyol.
13 . The resin foam according to claim 11 , wherein at least one kind of the compound having an OH group is polyethylene glycol.
14 . The resin foam according to claim 6 , wherein the amount of a hydrosilyl group in the compound (B) is 2 mol equivalent or more relative to an alkenyl group in the compound (A).
15 . The resin foam according to claim 1 , wherein the density is 10 kg/m 3 or more and lower than 500 kg/m 3 and the open cell coefficient is 80% or more.
16 . The resin foam according to claim 1 , comprising a foam having a density of 10 kg/m 3 or more and lower than 500 kg/m 3 , a thickness of 1 mm or more and lower than 100 mm, and an open cell coefficient of 80% or more.
17 . The resin foam according to claim 1 , which is obtained by uniting at least one member selected from the group consisting of a high water-absorbing resin and particles and fibers using the same.
18 . The resin foam according to claim 1 , wherein a water absorption expansion ratio represented by equation (2) when immersed in a physiological sodium chloride solution at 37° C. for 24 hours is lower than 50 vol %:
Water absorption expansion ratio=100×(Foam volume after immersion−Foam volume before immersion)/(Foam volume before immersion) (2).
19 . A process for producing the resin foam according to claim 1 , comprising:
mixing a resin composition obtained by adding an alkenyl group-containing compound (A), a hydrosilylation catalyst (C), and a foaming agent (D), and, depending on the case, another additive; and
adding and mixing a hydrosilyl group-containing compound (B) for injection foaming or spray foaming.