Radio wave absorption material and radio wave absorber
View Patent ↗A radio wave absorption material is characterized to be obtained by firing a ferrite material that is formed by adding an accessory component, 0.1 to 2 wt % of CoO, to an oxide magnetic material containing main components, 30 to 49.5 mol % of Fe 2 O 3 , 0.5 to 20 mol % of Mn 2 O 3 , 5 to 35 mol % of ZnO, 0.2 to 15 mol % of (Li 0.5 Fe 0.5 )O and MnO as the rest. In the above-mentioned composition, part of ZnO may be replaced with 20 mol % or less of CuO. This radio wave absorption material has high strength and humidity stability and has excellent radio wave absorption performance although low in cost.
1. A radio wave absorption material being characterized to be obtained by firing a ferrite material that is formed by adding 0.1 to 2 wt % of CoO to an oxide magnetic material containing 30 to 49.5 mol % of Fe 2 O 3 , 0.5 to 20 mol % of Mn 2 O 3 , 5 to 35 mol % of ZnO, 0.2 to 15 mol % of (Li 0.5 Fe 0.5 )O and MnO as the rest.
2. The radio wave absorption material according to claim 1 , wherein said oxide magnetic material contains 20 mol % or less of CuO.
3. The radio wave absorption material according to claim 1 , containing at least one of 0.001 to 0.5 wt % of Al 2 O 3 , 0.005 to 1.0 wt % of NiO and 0.005 to 0.4 wt % of Cr 2 O 3 .
4. The radio wave absorption material according to claim 1 , containing at least one of 0.002 to 0.095 wt % of a sulfur compound in terms of SO 3 and 0.002 to 0.08 wt % of a chlorine compound in terms of Cl.
5. The radio wave absorption material according to claim 1 , containing at least one of 0.002 to 0.3 wt % of SiO 2 and 0.003 to 0.3 wt % of CaO.
6. The radio wave absorption material according to claim 5 , wherein in the case that said material contains both SiO 2 and CaO, the total amount thereof is 0.5 wt % or less.
7. The radio wave absorption material according to claim 1 , containing a 0.001 to 0.08 wt % of a phosphor compound in terms of P 2 O 5 .
8. A radio wave absorber formed of said radio wave absorption material according to claim 1 .
9. The radio wave absorber according to claim 8 , wherein the reflection coefficient thereof for a radio wave of 30 MHz at a thickness of 8 mm or less is −20 dB or less.