Compositions and methods for resin-based wood glues
View Patent ↗A method for extending resin-based wood glues, particularly condensation polymer resin-based glues, comprises the steps of (i) providing an aqueous extender composition comprising 20% to 50% by weight of alkali metal silicate and 1% to 25% by weight of polyhydric alcohol, preferably a sugar such as sucrose, (ii) providing a solution comprising a resin and (iii) blending the aqueous extender and the solution together to form a glue. The extended glues are suitable for preparing water resistant processed wooden panels such as plywood or chipboard with reduced need for resin. The extended glues do not set excessively rapidly, allowing time for the processing of the wood composites.
1. A method for the preparation of a wood glue comprising from 4% to 60% by weight of a resin, the method comprising the steps of (i) providing an aqueous extender composition comprising from 20% to 50% by weight of alkali metal silicate and from 1% to 25% by weight of polyhydric alcohol, (ii) providing a solution comprising a resin and (iii) blending the aqueous extender composition of step (i) and the solution of step (ii) together to form the wood glue,
wherein the polyhydric alcohol has a solubility of at least 30% by weight in water.
2. A method for the preparation of a wood glue comprising from 4% to 60% by weight of a resin, the method comprising the steps of (i) providing an aqueous extender composition comprising from 20% to 50% by weight of alkali metal silicate and from 1% to 25% by weight of a polyhydric alcohol comprising sugar, (ii) providing a solution comprising a resin and (iii) blending the aqueous extender composition of step (i) and the solution of step (ii) together to form the wood glue.
3. A method according to claim 2 wherein the polyhydric alcohol consists essentially of sucrose.
4. A method according to claim 3 wherein the alkali metal silicate has a molar ratio of alkali metal oxide to SiO 2 expressed as SiO 2 /M 2 O, where M represents the alkali metal, from 0.9 to 3.7.
5. A method according to claim 4 wherein the alkali metal silicate is sodium silicate, potassium silicate or a mixture thereof.
6. A method according to claim 3 wherein the resin is a condensation polymer resin, preferably a resin selected from the group consisting of urea formaldehyde, phenol formaldehyde, melamine formaldehyde and mixtures thereof, more preferably phenol formaldehyde.
7. A glue comprising from 4% to 60% by weight of resin and from 0.5% to 50% by weight of an aqueous extender, the extender comprising from 20% to 50% by weight of alkali metal silicate and from 1% to 25% by weight of polyhydric alcohol, wherein the alkali metal silicate is selected from the group consisting of sodium silicate, potassium silicate or a mixture thereof, wherein the alkali metal silicate has a molar ratio of alkali metal oxide to SiO 2 expressed as SiO 2 /M 2 O, where M represents the alkali metal, from 0.9 to 3.7, and wherein the polyhydric alcohol has a solubility of at least 30% by weight in water.
8. A glue comprising from 4% to 60% by weight of resin, from 0.1% to 25%, by weight of alkali metal silicate and from 0.05% to 12.5% by weight of polyhydric alcohol, wherein the polyhydric alcohol has a solubility of at least 30% by weight in water.
9. A glue according to claim 8 wherein the alkali metal silicate has a molar ratio of alkali metal oxide to SiO 2 , expressed as SiO 2 /M 2 O, where M represents the alkali metal, from 0.9 to 3.7.
10. A glue according to claim 9 wherein the alkali metal silicate is sodium silicate, potassium silicate or a mixture thereof.
11. A glue comprising from 4% to 60% by weight of resin, from 0.1% to 25%, by weight of alkali metal silicate and from 0.05% to 12.5% by weight of a polyhydric alcohol comprising sugar, wherein the alkali metal silicate has a molar ratio of alkali metal oxide to SiO 2 , expressed as SiO 2 /M 2 O, where M represents the alkali metal, from 0.9 to 3.7 and wherein the alkali metal silicate is sodium silicate, potassium silicate or a mixture thereof.
12. A glue according to claim 11 wherein the polyhydric alcohol consists essentially of sucrose.
13. A glue according to claim 12 wherein the resin is a condensation polymer resin, preferably a resin selected from the group consisting of urea formaldehyde, phenol formaldehyde, melamine formaldehyde and mixtures thereof, more preferably phenol formaldehyde.
14. A glue according to claim 13 comprising up to 25% by weight of solid particulate water-insoluble filler.
15. A method for preparing wooden composites comprising the steps of (i) providing a glue according to claim 13 , (ii) providing particles or sheets of wood and (iii) gluing together the particles or sheets of wood with the glue.