Process for manufacturing a part made of a ceramic matrix composite containing matrix phases for healing and deflecting cracks
View Patent ↗The method comprises the steps of: forming a porous fiber-reinforcing structure; introducing into the pores of the fiber structure powders containing elements for constituting the composite material matrix; and forming at least a main fraction of the matrix from said powders by causing a reaction to take place between said powders or between at least a portion of said powders and at least one delivered additional element; the powders introduced into the fiber structure and the delivered additional element(s) comprising elements that form at least one healing discontinuous matrix phase including a boron compound and at least one discontinuous matrix phase including a crack-deflecting compound of lamellar structure. At least a main fraction of the matrix is formed by chemical reaction between the powders introduced into the fiber structure and at least one delivered additional element, or by sintering the powders.
1. A method of fabricating a part of composite material having a fiber reinforcement densified with a ceramic matrix, the method comprising the steps of:
forming a three-dimensional porous fiber structure to constitute the fiber reinforcement for the part to be fabricated;
providing a suspension of powders in a liquid, the powders having a mean dimension of less than 1 μm and including powder of at least one boron-containing compound and powder of at least one of carbon, silicon carbide and titanium carbide;
contacting said three-dimensional porous fibrous structure with said suspension to introduce said powders into the pores of the previously formed three-dimensional porous fiber structure; and
forming at least a main fraction of the matrix by chemical reaction between at least a portion of said powders and at least one delivered additional element selected from silicon and titanium, with both silicon and titanium being present in said powders and at least one delivered additional element taken together;
said chemical reaction being achieved by infiltrating the fiber structure with at least one of molten silicon, molten titanium and molten titanium-containing alloy, in order to form a matrix comprising at least one healing discontinuous matrix phase from said boron compound and at least one crack-deflecting discontinuous matrix phase of Ti 3 SiC 2 , said crack-deflecting discontinuous phase of Ti 3 SiC 2 being obtained at least in part by chemical reaction between silicon carbide in powder form, carbon and molten titanium or molten titanium-containing alloy or molten silicon.
2. A method according to claim 1 , wherein said powders introduced into the fiber structure comprise at least the elements B, C, and Ti, and at least the element Si is delivered in the form of molten silicon.
3. A method according to claim 1 , wherein said powders introduced into the fiber structure comprise at least the elements B, C, and Ti, and the element Si and then the element Ti are delivered successively in the form respectively of molten silicon and of molten titanium or titanium-containing alloy.
4. A method according to claim 2 , wherein said powders introduced into the fiber structure comprise titanium carbide and boron carbide.
5. A method according to claim 1 , wherein said powders introduced into the fiber structure comprise at least the elements B, C, and Si, and at least the element Ti is delivered in the form of molten titanium or a molten alloy containing titanium.
6. A method according to claim 1 , wherein said powders introduced into the fiber structure comprise at least the elements B, C, and Si, and the element Ti and then the element Si are delivered successively in the form respectively of molten titanium or a molten alloy containing titanium, and of molten silicon.
7. A method according to claim 5 , wherein said powders introduced in the fiber structure comprise a silicon carbide and a boron carbide.
8. A method according to claim 1 , wherein said powders introduced into the fiber structure comprise at least the elements B and C, and at least the elements Si and Ti are delivered simultaneously in the form of molten silicon and titanium or titanium alloy.
9. A method of fabricating a part of composite material having a fiber reinforcement densified with a ceramic matrix, the method comprising the steps of:
forming a three-dimensional porous fiber structure to constitute the fiber reinforcement for the part to be fabricated;
providing a suspension of powders in a liquid, the powders having a mean dimension of less than 1 μm and including powder of at least one boron-containing compound and powder of at least one of carbon, silicon carbide and titanium carbide;
contacting said three-dimensional porous fibrous structure with said suspension to introduce said powders into the pores of the previously formed three-dimensional porous fiber structure; and
forming at least a main fraction of the matrix by chemical reaction between at least a portion of said powders and at least one delivered additional element selected from silicon and titanium, with both silicon and titanium being present in said powders and at least one delivered additional element taken together;
said chemical reaction being achieved by infiltrating the fiber structure with at least one of molten silicon, molten titanium and molten titanium-containing alloy, in order to form a matrix comprising at least one healing discontinuous matrix phase from said boron compound and at least one crack-deflecting discontinuous matrix phase of Ti 3 SiC 2 ,
wherein said powders introduced into the fiber structure comprise at least the elements B, C, and Ti, and the element Si and then the element Ti are delivered successively in the form respectively of molten silicon and of molten titanium or titanium-containing alloy, or wherein said powders introduced into the fiber structure comprises at least the element B, C, and Si, and the element Ti and then the element Si are delivered successively in the form respectively of molten titanium or a molten alloy containing titanium, and of molten silicon.
10. A method of fabricating a part of composite material having a fiber reinforcement densified with a ceramic matrix, the method comprising the steps of:
forming a three-dimensional porous fiber structure to constitute the fiber reinforcement for the part to be fabricated;
providing a suspension of powders in a liquid, the powders having a mean dimension of less than μm and including powder of at least one boron-containing compound and powder of at least one of carbon, silicon carbide and titanium carbide;
contacting said three-dimensional porous fibrous structure with said suspension to introduce said powders into the pores of the previously formed three-dimensional porous fiber structure; and
forming at least a main fraction of the matrix by chemical reaction between at least a portion of said powders and at least titanium, and silicon being present in said powders;
said chemical reaction being achieved by infiltrating the fiber structure with at least one of molten titanium and molten titanium-containing alloy, in order to form a matrix comprising at least one healing discontinuous matrix phase from said boron compound and at least one crack-deflecting discontinuous matrix phase of Ti 3 SiC 2 , said crack-deflecting discontinuous phase of Ti 3 SiC 2 being obtained at least in part by chemical reaction between silicon carbide in powder form, carbon and molten titanium or molten titanium-containing alloy.
11. A method of fabricating a part of composite material having a fiber reinforcement densified with a ceramic matrix, the method comprising the steps of:
forming a three-dimensional porous fiber structure to constitute the fiber reinforcement for the part to be fabricated;
providing a suspension of powders in a liquid, the powders having a mean dimension of less than 1 μm and including powder of at least one boron-containing compound and powder of at least one of carbon, silicon carbide and titanium carbide;
contacting said three-dimensional porous fibrous structure with said suspension to introduce said powders into the pores of the previously formed three-dimensional porous fiber structure; and
forming at least a main fraction of the matrix by chemical reaction between at least a portion of said powders and at least one delivered additional element selected from silicon and titanium, with both silicon and titanium being present in said powders and at least one delivered additional element taken together;
said chemical reaction being achieved by infiltrating the fiber structure with at least one of molten titanium and molten titanium-containing alloy, in order to form a matrix comprising at least one healing discontinuous matrix phase from said boron compound and at least one crack-deflecting discontinuous matrix phase of Ti 3 SiC 2 , said crack-deflecting discontinuous phase of Ti 3 SiC 2 being obtained at least in part by chemical reaction between silicon carbide in powder form, carbon and molten titanium or molten titanium-containing alloy.