Lubricant for run flat tire system
View Patent ↗Lubricant compositions as well as methods and articles utilizing the lubricant compositions that comprise a polyoxyalkene as a lubricating agent, between 4 wt. % and 7.5 wt. % of silica as a thickening agent and an inorganic thixotropic-enhancing metal compound added in an amount of, for example, at least 20 ppm, by weight or alternatively, between 1 ppm and 2 wt. %. The silica may be fumed silica. Examples of the metal compound include KOH, NaOH, KCl, CaCl 2 , MgCl 2 , CaO, MgO, Mg(OH) 2 or combinations thereof. A tire is also included, comprising a radially inner face designed to be opposite a wheel rim on which it is designed to be mounted, wherein the radially inner face is provided with the lubricant composition described above.
1. A lubricant composition, comprising:
a polyoxyalkene as a lubricating agent;
between 4 wt. % and 7.5 wt. % of silica as a thickening agent;
no more than 1% water; and
between 300 ppm and 2 wt. % of an inorganic thixotropic-enhancing metal oxide, wherein a metal component of the thixotropic-enhancing metal oxide is selected from alkali metals, alkaline earth metals, iron, cobalt, nickel, copper, aluminum or combinations thereof, wherein the lubricant composition viscosity is between 10 Pa-s and 60 Pa-s measured at 20° C. with a shear rate of 10 s −1 , and wherein the inorganic thixotropic-enhancing metal oxide provides an increase in a recovered threshold stress value TS2 of the lubricant composition to at least about 90% of the initial threshold stress value TS1.
2. The composition of claim 1 , wherein the inorganic thixotropic-enhancing metal oxide is added in an amount of between 300 ppm and 700 ppm, by weight.
3. The composition of claim 1 , wherein the thixotropic-enhancing metal oxide is selected from CaO, MgO or combinations thereof.
4. The composition of claim 1 , wherein the composition comprises less than 300 ppm by weight of water.
5. The composition of claim 1 , wherein the composition comprises less than 700 ppm by weight of water.
6. The composition of claim 1 , wherein the composition comprises no water.