Process for making high-pressure sheet gasketing materials
View Patent ↗A method for making high-pressure sheet gasketing material is provided that employs an elastomer, such as natural rubber and/or acylonitrile-butadiene rubber. Tert-butyl acetate is added to dissolve the elastomer. Other components may then be mixed with the dissolved elastomer and may include, for example, antioxidants, colorants, curing agents, curing accelerators, reinforcing fillers, and fibers such as organic and/or mineral fibers. The resulting dough may be formed into a high-pressure sheets, for use as gasketing material, using a two-roll sheeter machine, or the like.
1. A process for making a dough that may be used to form compressed sheet gasketing material, the process consisting essentially of:
mixing a quantity of tert-butyl acetate with a quantity of elastomer so that said elastomer is substantially dissolved in said tert-butyl acetate; and
mixing with said dissolved elastomer a quantity of filler and a quantity of fiber.
2. The process of claim 1 wherein said elastomer is comprised of a natural rubber.
3. The process of claim 1 wherein said elastomer is comprised of acrylonitrile-butadiene rubber.
4. The process of claim 1 wherein said elastomer is comprised of a mixture of natural rubber and acrylonitrile-butadiene rubber.
5. The process of claim 1 wherein said elastomer is selected from the group consisting of natural rubber, styrene-butadiene rubber, chloroprene rubber, fluoroelastomer, nitrile rubber, and acrylonitrile-butadiene rubber.
6. The process of claim 1 wherein said filler is comprised of an inorganic material.
7. The process of claim 6 wherein said filler is selected from the group consisting of clays and minerals.
8. The process of claim 1 wherein said fiber is an organic fiber.
9. The process of claim 8 wherein said fiber is selected from the group consisting of polyaramide, nylon, polyacrylate, and cellulose.
10. The process of claim 1 wherein said fiber is an inorganic fiber.
11. The process of claim 10 wherein said fiber is selected from the group consisting of sepiolite, asbestos, fiberglass, and carbon fibers.
12. The process of claim 1 further comprising:
mixing with said dissolved elastomer a quantity of at least one additional material selected from the group consisting of an antioxidant, a colorant, a curing agent, and a curing accelerator.
13. The process of claim 12 wherein said colorant includes zinc oxide.
14. The process of claim 12 wherein said curing agent includes sulfur.
15. The process of claim 12 wherein said curing accelerator includes tetramethyithiuram disulfide.
16. The process of claim 1 wherein said quantity of tert-butyl acetate approximates 20%-50% by weight of the dough.
17. The process of claim 1 where said quantity of elastomer approximates 10%-21% by weight.
18. The process of claim 1 wherein said quantity of filler approximates 40%-80% by weight.
19. The process of claim 1 wherein said quantity of fiber approximates 10%-40% by weight.
20. A process for making a dough that may be used to form sheet gasketing material, the process consisting essentially of:
mixing a quantity of solvent from the family of solvents that includes tert-butyl acetate, n-propyl acetate, n-butyl acetate, sec-butyl acetate, isopropyl acetate, pentyl acetate, and isopentyl acetate with a quantity of elastomer so that said elastomer is substantially dissolved in said solvent; and
mixing with said dissolved elastomer a quantity of filler and a quantity of fiber.
21. A composition that may be used to form compressed sheet gasketing material, the composition at least comprising:
a quantity of tert-butyl acetate;
a quantity of elastomer;
a quantity of filler; and
a quantity of fiber.
22. The composition of claim 21 wherein said quantity of tert-butyl acetate approximates 20%-50% by weight of the dough.
23. The composition of claim 21 wherein said quantity of elastomer approximates 10%-21% by weight.
24. The composition of claim 21 wherein said quantity of filler approximates 40%-80% of weight and said quantity of fiber approximates 10%-40% by weight.
25. A process for making a dough that may be used to form sheet gasketing material, the process consisting essentially of:
mixing a quantity of a solvent, having a flashpoint within the range of approximately 58° F. to 100° F., with a quantity of elastomer so that said elastomer is substantially dissolved in said solvent; and
mixing with said dissolved elastomer a quantity of filler and a quantity of fiber.