Transparent electroconductive film and process for producing the same
View Patent ↗In a transparent electroconductive film including a transparent substrate and a transparent electroconductive oxide layer disposed on the transparent substrate, when the transparent electroconductive oxide layer is composed of zinc oxide, the surface resistivity of the transparent electroconductive oxide layer increases with time and thus it has been difficult to obtain a transparent electroconductive film stable against an environmental variation. Consequently, hard carbon films are provided on the surfaces of a transparent electroconductive oxide layer including at least one layer and containing zinc oxide as a main component in “the order of transparent substrate-hard carbon film-transparent electroconductive oxide layer-hard carbon film” or “the order of hard carbon film-transparent substrate-transparent electroconductive oxide layer-hard carbon film”. Alternatively, an organosilicon compound covering layer is provided on a surface of the transparent electroconductive oxide layer. Thereby, the water contact angle can be 75 degrees or more, and an increase in the resistivity of the transparent electroconductive oxide layer can be suppressed.
1. A transparent electroconductive film comprising;
a transparent substrate;
a second hard carbon film;
a transparent electroconductive oxide layer having an electroconductive side surface, which layer includes at least one layer and contains zinc oxide as a main component; and
a first hard carbon film;
arranged in that order,
wherein the first hard carbon film and the second hard carbon film each have a thickness in a range of 10 to 300 Å, and
wherein the first hard carbon film has electrical conductivity and is disposed directly on the electroconductive side surface of the transparent electroconductive oxide layer.
2. The transparent electroconductive film according to claim 1 , wherein the first hard carbon film and the second hard carbon film satisfy (A) to (C) below at the same time:
(A) a hydrogen atom that forms a carbon-hydrogen bond;
(B) a refractive index in a range of 1.65 to 1.95; and
(C) a proportion of SP 3 in bonds measured by X-ray photoelectron spectroscopy of 65% or more.
3. A process for producing the transparent electroconductive film according to claim 1 , which comprises forming the first hard carbon film and the second hard carbon film by radio-frequency plasma chemical vapor deposition (CVD), wherein a methane gas and a hydrogen gas used as raw material gases are prepared as a mixed gas so as to satisfy the relationship represented by formula 1:
0.04≦V(CH 4 )/(V(CH 4 )+V(H 2 ))≦0.1 (Formula 1)
wherein V(CH 4 ) represents a flow rate of the methane gas and V(H 2 ) represents a flow rate of the hydrogen gas.
4. A process for producing the transparent electroconductive film according to claim 2 , which comprises forming the first hard carbon film and the second hard carbon film by radio-frequency plasma chemical vapor deposition (CVD), wherein a methane gas and a hydrogen gas used as raw material gases are prepared as a mixed gas so as to satisfy the relationship represented by formula 1:
0.04≦V(CH 4 )/(V(CH 4 )+V(H 2 ))≦0.1 (Formula 1)
wherein V(CH 4 ) represents a flow rate of the methane gas and V(H 2 ) represents a flow rate of the hydrogen gas.