Low iron transmission float glass for solar cell applications and method of making same
Certain example embodiments of this invention relate to a high transmission low iron glass, which is highly oxidized and made using the float process, for use in photovoltaic devices such as solar cells or the like. In certain example embodiments, the glass composition used for the glass is made via the float process using an extremely high and positive batch redox in order to reduce % FeO to a low level and permit the glass to consistently realize a combination of high visible transmission (Lta or T vis ), high infrared (IR) transmission, and high total solar (TS) transmission. The glass substrate may be patterned or not patterned in different example embodiments of this invention.
1. A solar cell comprising:
a glass substrate;
first and second conductive layers with at least a photoelectric film provided therebetween;
wherein a composition of the glass substrate comprises:
Ingredient
wt. %
SiO 2
67-75%
Na 2 O
10-20%
CaO
5-15%
total iron (expressed as Fe 2 O 3 )
<=0.1%
% FeO
<=0.005
glass redox
<=0.08
antimony oxide
0 to less than 0.01%
cobalt oxide
0%
cerium oxide
0%
wherein the glass substrate has visible transmission of at least 90%, TS transmission of at least 90%; a transmissive a* color value of −1.0 to +1.0, a transmissive b* color value of from −0.5 to +1.5.
2. The solar cell of claim 1 , wherein the glass substrate comprises:
% FeO
<=0.003%
glass redox
<=0.06.
3. The solar cell of claim 1 , wherein the glass substrate has a % TS of at least 91% and comprises:
% FeO
<=0.002%
glass redox
<=0.04.
4. The solar cell of claim 1 , wherein the glass substrate comprises from 0.30 to 0.50% SO 3 .
5. The solar cell of claim 1 , wherein the glass substrate contains no more than 2 ppm of at least four of: erbium oxide, nickel oxide, neodymium oxide, chromium oxide, and selenium.