View Patent ↗A catalytic system usable for the copolymerization of at least one conjugated diene and at least one monoolefin, a process for preparing this catalytic system, a process for preparing a copolymer of a conjugated diene and at least one monoolefin using said catalytic system, and said copolymer are described. This catalytic system includes: (i) an organometallic complex represented by the following formula: {[P(Cp)(Fl)Ln(X)(L X )} p (1) where Ln represents a lanthanide atom to which is attached a ligand molecule comprising cyclopentadienyl Cp and fluorenyl Fl groups linked to one another by a bridge P of the formula MR 1 R 2 , M is an element from column IVa of Mendeleev's periodic table and R 1 and R 2 each represent alkyl groups of 1 to 20 carbon atoms or cycloalkyl or phenyl groups of 6 to 20 carbon atoms, X represents a halogen atom, L represents an optional complexing molecule, such as an ether, and optionally a substantially less complexing molecule, such as toluene, p is a natural integer greater than or equal to 1 and x is greater than or equal to 0, and (ii) a co-catalyst selected from alkylmagnesiums, alkyllithiums, alkylaluminums, Grignard reagents and mixtures of these constituents.
1. A copolymer of at least one conjugated diene and at least one alpha-olefin having from 3 to 18 carbon atoms, wherein said copolymer fulfils the following conditions:
the number-average molecular mass of said copolymer is greater than 60,000 g/mol,
said copolymer comprises units resulting from said conjugated diene(s) in a molar content of greater than 40% and less than or equal to 90%, and units resulting from said alpha-olefin(s) in a molar content of less than 60% and greater than or equal to 10%,
said units resulting from said conjugated diene(s) have a trans-1,4 linkage content of greater than 70%,
said copolymer is devoid of cyclic units, and
said copolymer is such that each unit resulting from said alpha-olefin(s) is inserted in the chain of said copolymer between two units resulting from said or each conjugated diene.
2. The copolymer according to claim 1 , which comprises units resulting from said conjugated diene(s) in a molar content of greater than 60% and less than or equal to 80%, and units resulting from said alpha-olefin(s) in a molar content of less than 40% and greater than or equal to 20%.
3. The copolymer according to claim 1 , which consists of a copolymer of a conjugated diene and an alpha-olefin having from 3 to 18 carbon atoms.
4. The copolymer according to claim 1 , which consists of a terpolymer of a conjugated diene, ethylene and an alpha-olefin having from 3 to 18 carbon atoms.