Polymer compositions of bromostyrenes having controlled molecular weight
View Patent ↗A controlled molecular weight polymer of styrene is provided having bromine substituted thereon. Control of molecular weight is achieved by the use of alpha-methyl styrene dimer as a chain transfer agent. The brominated polymer of styrene is useful as a flame retardant, particularly for polyamides giving improved properties including color retention after molding.
1. A polymer composition comprising at least one polyamide and polymers of ar-bromostyrene monomers having the following general structure
where R is H and x is 3, where the polymers have an assigned weight average molecular weight (MW) compared with a polystyrene standard as measured by gel permeation chromatography of from about 11,000 to about 60,000, wherein the polymers further comprise residues of α-methyl styrene dimer.
2. The polymers of claim 1 further comprising units derived from copolymerization with a comonomer selected from the group consisting of glycidyl (meth)acrylate, maleic anhydride, hydroxyethylmethacrylate, acrylic acid ar-amino substituted styrene, styrene sulfonic acid, salts of styrene sulfonic acid and mixtures thereof.
3. The polymers of claim 1 further comprising units derived from copolymerization with a comonomer selected from the group consisting of styrene, butadiene acrylonitrile, methyl-(meth)acrylate, divinyl benzene, isoprene, n-butylacrylate, α-methyl styrene, p-methyl styrene and mixtures thereof.
4. The polymer composition of claim 1 in which the at least one polyamide has a melt temperature above about 280° C.
5. The polymer composition of claim 1 wherein the at least one polyamide is independently selected from the group consisting of: polyamide-4,6, polyamide-4,8, polyamide-4,9, polyamide-4,10, polyamide-4,11 polyamide-4,12, polyamide-4,13, polyamide-4,14, semi-aromatic polyamides, and mixtures thereof.
6. The polymer composition of claim 5 in which the at least one polyamide has a melt temperature above about 280° C.
7. A polymer composition comprising at least one polyamide and polymers of ar-bromostyrene monomers having the following general structure
where R is H and x is 3, where the polymers have an assigned weight average molecular weight of from about 11,000 to about 60,000, wherein the polymers retain at least 88% of their mass after 20 minutes and at least 85% of their mass after 30 minutes when a 10 mg specimen is held at 330° C. under a nitrogen atmosphere.
8. The composition of claim 7 in which the at least one polyamide has a melt temperature above about 280° C.
9. The composition of claim 7 wherein the polyamide is independently selected from the group consisting of: polyamide-4,6, polyamide-4,8, polyamide-4,9, polyamide-4,10, polyamide-4,11 polyamide-4,12, polyamide-4,13, polyamide-4,14 semi-aromatic polyamides, and mixtures thereof.
10. The polymer composition of claim 1 wherein the polymers have an assigned weight average molecular weight compared with a polystyrene standard as measured by gel permeation chromatography of from about 15,000 to about 20,000.
11. The polymer composition of claim 5 wherein the semi-aromatic polyamides are selected from the group consisting of polyamide-6,6/6,T, polyamide-4,6/4,T/4,1, polyamide-9,T, polyamide-12,T and mixtures thereof.
12. The composition of claim 9 wherein the semi-aromatic polyamides are selected from the group consisting of polyamide-6,6/6,T, polyamide-4,6/4,T/4,1, polyamide-9,T, polyamide-12,T and mixtures thereof.