Process for controlling the molecular weight of polymers of bromostyrenes
View Patent ↗A controlled molecular weight polymer of styrene is provided having bromine substituted thereon. Control of molecular weight is achieved by the use of alpha-methyl styrene dimer as a chain transfer agent. The brominated polymer of styrene is useful as a flame retardant, particularly for polyamides giving improved properties including color retention after molding.
1. A process to control the molecular weight of bromostyrene polymers in which α-methyl styrene dimer is used as a chain transfer agent, comprising the steps of:
(a) providing an essentially solventless blend of:
(i) ar-bromostyrene monomers having the following general structure
where R is H and x is 3, where the polymers have an assigned weight average molecular weight (MW) compared with a polystyrene standard as measured by gel permeation chromatography of from about 11,000 to about 60,000;
(ii) a polymerization initiator; and
(iii) α-methyl styrene dimer,
(b) feeding the monomer/polymerization initiator blend into a reaction vessel;
(c) reacting the monomer/polymerization initiator blend under conditions effective to polymerize at least about 80% of the monomers in a time of between about 1 minute and about 20 minutes; and
(d) removing the polymerized bromostyrenes from the reaction vessel.
2. The process of claim 1 wherein the bromostyrene polymers retain at least 88% of their mass after 20 minutes and at least 85% of their mass after 30 minutes when a 10 mg specimen is held at 330° C. under a nitrogen atmosphere.
3. The process of claim 2 wherein the bromostyrene polymers have an assigned weight average molecular weight compared with a polystyrene standard as measured by gel permeation chromatography of from about 15,000 to about 20,000.
4. The process of claim 1 wherein the bromostyrene polymers further comprise residues of α-methyl styrene dimer.