Pasted zinc electrode for rechargeable nickel-zinc batteries
View Patent ↗Active material for a negative electrode of a rechargeable zinc alkaline electrochemical cell is made with zinc metal particles coated with tin and/or lead. The zinc particles may be coated by adding lead and tin salts to a slurry containing zinc particles, a thickening agent and water. The remaining zinc electrode constituents such as zinc oxide (ZnO), bismuth oxide (Bi 2 O 3 ), a dispersing agent, and a binding agent such as Teflon are then added. The resulting slurry/paste has a stable viscosity and is easy to work with during manufacture of the zinc electrode. Further, the zinc electrode is much less prone to gassing when cobalt is present in the electrolyte. Cells manufactured from electrodes produced in accordance with this invention exhibit much less hydrogen gassing, by as much as 60-80%, than conventional cells. The cycle life and shelf life of the cells is also enhanced, as the zinc conductive matrix remains intact and shelf discharge is reduced.
1. A rechargeable nickel zinc cell comprising:
a negative zinc electrode having zinc powder particles, wherein said zinc powder particles are less than about 100 microns in size and are coated with a coating consisting essentially of tin; and
a nickel positive electrode comprising a material selected from the group consisting of cobalt metal, cobalt compound, and combinations thereof,
wherein the tin comprises less than about 1% by weight of the negative zinc electrode active material.
2. The nickel zinc cell of claim 1 , wherein the negative zinc electrode active material further comprises zinc oxide, bismuth oxide, and a binding agent.
3. The nickel zinc cell of claim 1 , wherein the cobalt compound is selected from the group consisting of cobalt oxide, cobalt hydroxide, cobalt oxyhydroxide and combinations thereof, wherein the cobalt compound is coated on nickel hydroxide particles.
4. The nickel zinc cell of claim 1 , wherein the positive electrode comprises a material selected from the group consisting of cobalt metal, cobalt oxide, cobalt hydroxide, cobalt oxyhydroxide, and combinations thereof, and wherein the positive electrode further comprises nickel hydroxide particles.
5. The nickel zinc cell of claim 1 , wherein the zinc powder particles are less than about 40 microns in size.
6. An as-fabricated zinc electrode, said electrode comprising:
an active material layer comprising (a) zinc oxide, (b) zinc alloy particles coated with a coating consisting essentially of tin, (c) bismuth oxide, and (d) a binding agent; and
a conductive substrate layer;
wherein the tin comprises less than about 1% by weight of the active material layer and, wherein the zinc alloy particles comprise an alloy of zinc with an alloying element selected from the group consisting of bismuth, indium, and combinations thereof, and wherein the zinc alloy particles are less than about 100 micrometers in size.
7. The nickel zinc cell of claim 1 , wherein the zinc powder particles are zinc alloy particles comprising an alloy of zinc with an alloying element selected from the group consisting of bismuth, indium, and combinations thereof.
8. The nickel zinc cell of claim 7 , wherein the zinc powder particles are less than about 40 micron in size.
9. The zinc electrode of claim 6 , wherein the zinc alloy particles are less than about 40 micron in size.
10. The nickel zinc cell of claim 1 , wherein the zinc powder particles are less than about 25 micron in size.
11. The zinc electrode of claim 6 , wherein the zinc alloy particles are less than about 25 micron in size.
12. A rechargeable nickel zinc cell comprising:
a negative zinc electrode having zinc powder particles, wherein said zinc powder particles are less than about 100 microns in size and are coated with a coating consisting essentially of lead, wherein the lead comprises less than about 0.05% by weight of the negative zinc electrode active material; and
a nickel positive electrode comprising a material selected from the group consisting of cobalt metal, cobalt compound, and combinations thereof.
13. A rechargeable nickel zinc cell comprising:
a negative zinc electrode having zinc powder particles, wherein said zinc powder particles are less than about 100 microns in size and are coated with a coating consisting essentially of lead and tin, wherein the tin comprises less than about 1% by weight of the negative zinc electrode active material and wherein the lead comprises less than about 0.05% by weight of the negative zinc electrode active material; and
a nickel positive electrode comprising a material selected from the group consisting of cobalt metal, cobalt compound, and combinations thereof.
14. A rechargeable nickel zinc cell comprising:
a negative zinc electrode having zinc alloy powder particles, wherein said zinc alloy powder particles comprise an alloy of zinc with bismuth and indium, are less than about 100 microns in size, and are coated with a coating consisting essentially of a material selected from the group consisting of lead, tin, and combinations thereof; and
a nickel positive electrode comprising a material selected from the group consisting of cobalt metal, cobalt compound, and combinations thereof.
15. An as-fabricated zinc electrode, said electrode comprising:
an active material layer comprising (a) zinc oxide, (b) zinc alloy particles coated with a coating consisting essentially of lead, (c) bismuth oxide, and (d) a binding agent; and
a conductive substrate layer;
wherein the lead comprises less than about 0.05% by weight of the active material layer, and wherein the zinc alloy particles comprise an alloy of zinc with an alloying element selected from the group consisting of bismuth, indium, and combinations thereof, and wherein the zinc particles are less than about 100 micrometers in size.
16. An as-fabricated zinc electrode, said electrode comprising:
an active material layer comprising (a) zinc oxide, (b) zinc alloy particles coated with a coating consisting essentially of tin and lead, (c) bismuth oxide, and (d) a binding agent; and
a conductive substrate layer;
wherein the tin comprises less than about 1% by weight of the active material layer and, and wherein the lead comprises less than about 0.05% by weight of the active material layer, wherein the zinc alloy particles comprise an alloy of zinc with an alloying element selected from the group consisting of bismuth, indium, and combinations thereof, and wherein the zinc particles are less than about 100 micrometers in size.