Low alloy steel for high-pressure hydrogen gas environment and container for high-pressure hydrogen
View Patent ↗Provided is a low alloy steel for high-pressure hydrogen gas environments, which contains, by mass percent, C: 0.15 to 0.60%, Si: 0.05 to 0.5%, Mn: 0.05 to 3.0%, P: not more than 0.025%, S: not more than 0.010%, Al: 0.005 to 0.10%, Mo: 0.5 to 3.0%, V: 0.05 to 0.30%, O (oxygen): not more than 0.01%, N: not more than 0.03%, and the balance Fe and impurities, and has tensile strength of not less than 900 MPa. This low alloy steel desirably contains B of 0.0003 to 0.003%, but in this case, N is limited to not more than 0.010%. It is desirable to contain at least one among Cr, Nb, Ti, Zr, and Ca. The contents of Mo and V desirably satisfy the following formula (1): [Mo(%)]·[V(%)] 0.2 ≧0.32 (1).
1. A container for high-pressure hydrogen made of a low alloy steel consisting of, by mass percent, C: 0.38 to 0.60%, Si: 0.05 to 0.5%, Mn: 0.05 to 3.0%, P: not more than 0.025%, S: not more than 0.010%, Al: 0.005 to 0.10%, Mo: 0.5 to 3.0%, V: 0.05 to 0.30%, O (oxygen): not more than 0.01%, N: not more than 0.03%, and the balance Fe and impurities, and the said steel having tensile strength of not less than 900 MPa, wherein the contents of Mo and V satisfy the following formula (1):
[Mo(%)]·[V(%)] 0.2 ≧0.4 (1).
2. A container for high-pressure hydrogen made of a low alloy steel consisting of, by mass percent, C: 0.38 to 0.60%, Si: 0.05 to 0.5%, Mn: 0.05 to 3.0%, P: not more than 0.025%, S: not more than 0.010%, Al: 0.005 to 0.10%, Mo: 0.5 to 3.0%, V: 0.05 to 0.30%, O (oxygen): not more than 0.01%, B: 0.0003 to 0.003%, N: not more than 0.010%, and the balance Fe and impurities, and the said steel having tensile strength of not less than 900 MPa, wherein the contents of Mo and V satisfy the following formula (1):
[Mo(%)]·[V(%)] 0.2 ≧0.4 (1).
3. A container for high-pressure hydrogen, made of a low alloy steel consisting of, by mass percent, C: 0.38 to 0.60%, Si: 0.05 to 0.5%, Mn: 0.05 to 3.0%, P: not more than 0.025%, S: not more than 0.010%, Al: 0.005 to 0.10%, Mo: 0.5 to 3.0%, V: 0.05 to 0.30%, O (oxygen): not more than 0.01%, N: not more than 0.03%, one element selected from Cr: 0.2 to 2.0%, Nb: 0.002 to 0.1%, Ti: 0.002 to 0.1%, Zr: 0.002 to 0.1% and Ca: 0.0003 to 0.01%, and the balance Fe and impurities, and the said steel having tensile strength of not less than 900 MPa, wherein the contents of Mo and V satisfy the following formula (1):
[Mo(%)]·[V(%)] 0.2 ≧0.4 (1).
4. A container for high-pressure hydrogen, made of a low alloy steel consisting of, by mass percent, C: 0.38 to 0.60%, Si: 0.05 to 0.5%, Mn: 0.05 to 3.0%, P: not more than 0.025%, S: not more than 0.010%, Al: 0.005 to 0.10%, Mo: 0.5 to 3.0%, V: 0.05 to 0.30%, O (oxygen): not more than 0.01%, B: 0.0003 to 0.003%, N: not more than 0.010%, one element selected from Cr: 0.2 to 2.0%, Nb: 0.002 to 0.1%, Ti: 0.002 to 0.1%, Zr: 0.002 to 0.1% and Ca: 0.0003 to 0.01%, and the balance Fe and impurities, and the said steel having tensile strength of not less than 900 MPa, wherein the content of Mo and V satisfy the following formula (1):
[Mo(%)]·[V(%)] 0.2 ≧0.4 (1).
5. A container for high-pressure hydrogen, made of a low alloy steel consisting of, by mass percent, C: 0.38 to 0.60%, Si: 0.05 to 0.5%, Mn: 0.05 to 3.0%, P: not more than 0.025%, S: not more than 0.010%, Al: 0.005 to 0.10%, Mo: 0.5 to 3.0%, V: 0.05 to 0.30%, O (oxygen): not more than 0.01%, N: not more than 0.03%, two elements selected from Cr: 0.2 to 2.0%, Nb: 0.002 to 0.1%, Ti: 0.002 to 0.1%, Zr: 0.002 to 0.1% and Ca: 0.0003 to 0.01%, and the balance Fe and impurities, and the said steel having a tensile strength of not less than 900 MPa, wherein the contents of Mo and V satisfy the following formula (1):
[Mo(%)]·[V(%)] 0.2 ≧0.40 (1).
6. A container for high-pressure hydrogen, made of a low alloy steel consisting of, by mass percent, C: 0.38 to 0.60%, Si: 0.05 to 0.5%, Mn: 0.05 to 3.0%, P: not more than 0.025%, S: not more than 0.010%, Al: 0.005 to 0.10%, Mo: 0.5 to 3.0%, V: 0.05 to 0.30%, O (oxygen): not more than 0.01%, B: 0.0003 to 0.003%, N: not more than 0.010%, two elements selected from Cr: 0.2 to 2.0%, Nb: 0.002 to 0.1%, Ti: 0.002 to 0.1%, Zr: 0.002 to 0.1% and Ca: 0.0003 to 0.01%, and the balance Fe and impurities, and the said steel having a tensile strength of not less than 900 MPa, wherein the contents of Mo and V satisfy the following formula (1):
[Mo(%)]·[V(%)] 0.2 ≧0.40 (1).