Fluoroelastomer composition containing process aid

1. A polyhydroxy curable fluoroelastomer composition comprising:

A) fluoroelastomer;

B) 0.05 to 10 parts by weight, per 100 parts by weight fluoroelastomer, of an aminosilicone fluid having a single primary amine group per polysiloxane molecule;

C) 0.1 to 20 parts by weight, per 100 parts by weight fluoroelastomer, of a polyhydroxy curative;

D) 0.1 to 10 parts by weight, per 100 parts by weight fluoroelastomer, of a cure accelerator; and

E) 0.5 to 30 parts by weight, per 100 parts by weight fluoroelastomer, of an acid acceptor.

2. A polyhydroxy curable fluoroelastomer composition of claim 1 wherein said fluoroelastomer is selected from the group consisting of copolymers of i) vinylidene fluoride with hexafluoropropylene; ii) vinylidene fluoride with hexafluoropropylene and tetrafluoroethylene; iii) vinylidene fluoride with perfluoro(methyl vinyl ether) and 2-hydropentafluoroethylene; iv) vinylidene fluoride with perfluoro(methyl vinyl ether), 2-hydropentafluoroethylene and tetrafluoroethylene; v) tetrafluoroethylene with propylene and 3,3,3-trifluoropropene; and vi) ethylene with tetrafluoroethylene, perfluoro(methyl vinyl ether) and 3,3,3-trifluoropropylene.

3. A polyhydroxy curable fluoroelastomer composition of claim 1 wherein said amino silicone has a number average molecular weight between 500 and 50,000.

4. A polyhydroxy curable fluoroelastomer composition of claim 3 wherein said amino silicone has a number average molecular weight between 1000 and 10,000.

5. A polyhydroxy curable fluoroelastomer composition of claim 1 wherein said amino silicone is present at a level of 0.1 to 1 parts by weight, per 100 parts by weight fluoroelastomer.

6. A curable fluoroelastomer composition of claim 1 wherein said polyhydroxy curative is selected from the group consisting of i) dihydroxy-, trihydroxy-, and tetrahydroxy-benzenes, -naphthalenes, and -anthracenes;

ii) bisphenols of the formula

where A is a stable divalent radical; x is 0 or 1; and n is 1 or 2; iii) dialkali salts of said bisphenols, iv) quaternary ammonium salts of said bisphenols, v) quaternary phosphonium salts of said bisphenols, vi) tertiary sulfonium salts of said bisphenols, and vii) esters of said bisphenols.

7. A curable fluoroelastomer composition of claim 1 wherein said cure accelerator is chosen from the group consisting of quaternary ammonium salts, tertiary sulfonium salts and quaternary phosphonium salts.