Physically modified extracellular matrix materials and uses thereof
View Patent ↗Described are expanded collagenous materials and methods for their preparation and use. Certain expanded collagenous materials can be prepared by treating a first collagenous material with an alkaline substance under conditions effective to expand the first collagenous material, and recovering the expanded material. Expanded materials can exhibit beneficial persistence and tissue generation characteristics when implanted, and can be used in the formation of highly porous medical implant bodies which can be compressed to fractions of their original volume and will thereafter substantially recover their original volume.
1. A method for preparing a compressible graft construct, comprising:
contacting a first extracellular matrix material with an alkaline aqueous liquid having a pH between 8 and 14 to form a second, expanded extracellular matrix material, said first extracellular matrix material comprising at least 80% by weight collagen on a dry weight basis, wherein said contacting is sufficient to denature collagen of the first extracellular matrix material such that denatured collagen is present in the second expanded extracellular matrix material, wherein said second expanded extracellular matrix material has a volume of at least 120% that of the volume of said first extracellular matrix material, and wherein said first extracellular matrix material is a sheet material, and wherein upon completion of said contacting, the expanded extracellular matrix material is a sheet material;
charging the expanded extracellular matrix material to a mold; and
drying the expanded extracellular matrix material to form the compressible graft construct.
2. The method of claim 1 , wherein said alkaline aqueous liquid comprises a source of hydroxide ions.
3. The method of claim 2 , wherein said source of hydroxide ions comprises sodium hydroxide.
4. The method of claim 1 , wherein said first extracellular matrix material is a decellularized tissue layer.
5. The method of claim 4 , wherein said first extracellular matrix material comprises submucosa.
6. The method of claim 1 , wherein said expanded extracellular matrix material is dried by lyophilization.
7. A method for preparing an implantable plug graft, comprising:
contacting a first extracellular matrix material with an alkaline aqueous liquid having a pH between 8 and 14 to form a second, expanded extracellular matrix material, wherein said contacting is sufficient to denature collagen of the first extracellular matrix material such that denatured collagen is present in the second expanded extracellular matrix material, wherein said second expanded extracellular matrix material has a volume of at least 120% that of the volume of said first extracellular matrix material; and wherein said first extracellular matrix material is a sheet material, and wherein upon completion of said contacting, the expanded extracellular matrix material is a sheet material; and
preparing a plug comprising the expanded extracellular matrix material.
8. The method of claim 7 , wherein said alkaline aqueous liquid comprises a source of hydroxide ions.
9. The method of claim 8 , wherein said source of hydroxide ions comprises sodium hydroxide.
10. The method of claim 7 , wherein said alkaline aqueous liquid has a pH in the range of 10 to 14.
11. The method of claim 7 , wherein said first extracellular matrix material is a decellularized tissue layer.
12. The method of claim 11 , wherein said first extracellular matrix material comprises submucosa.
13. The method of claim 7 , wherein said preparing comprises lyophilizing the expanded extracellular matrix material to form said plug as a foam plug.
14. The method of claim 7 , wherein said expanded extracellular matrix material has a volume of at least twice that of the first extracellular matrix material.
15. The method of claim 7 , wherein said preparing comprises casting the expanded extracellular matrix material.
16. The method of claim 7 , wherein said first extracellular matrix material comprises at least 80% collagen on a dry weight basis.