Curing or sealing compositions for concrete and cement formulations and processes for using the same
View Patent ↗Disclosed are wax emulsion compositions for curing or sealing concrete and cement formulations, methods for preparing and processes for using the same. The modifiers are applicable to curing or sealing membranes, used in roadways, highways, parking lots and other freshly placed or poured concrete surfaces to retain moisture and achieve high compressive strengths. This invention also relates to materials used to coat, spray, brush, roll etc. on conventional Portland cement concrete mix designs or other applied concrete mixes in formed structural shapes and transport road mix designs, providing an effective layer that controls and minimizes moisture loss from the mix to enable proper curing and achievement of desired compressive strengths. The compositions of the invention further provide for concrete and cement formulations having lower water soluble chloride content.
1. A process for curing or sealing concrete and cement formulations comprising:
a) combining into an emulsion, components comprising:
about 10 to about 40 wt % of a paraffin hydrocarbon wax, based upon the weight of the emulsion, about 0.01 to about 20 parts by weight of a saponifiable wax, per 100 parts of a paraffin wax, a saponifier, and about 0.1 to about 5 wt % of a dispersant, based upon the weight of the emulsion to form an aqueous emulsion;
b) applying the aqueous emulsion to a surface of the concrete or cement formulation; and
c) curing, sealing, or both curing and sealing, the concrete or cement formulation,
wherein the aqueous emulsion is free of synthetic polymers.
2. The process of claim 1 , further comprising heating the aqueous emulsion to a temperature of between about 185° F. (85° C.) to about 205° F. (96.1° C.), then homogenizing the mixture prior to applying the aqueous emulsion.
3. The process of claim 1 , wherein the aqueous emulsion penetrates the surface of concrete or cement formulation to a depth of at least ¾ inches.
4. The process of claim 1 , wherein the aqueous emulsion is free of olefin-maleic anhydride derivatives.
5. The process of claim 1 , wherein the aqueous emulsion consists essentially of about 10 to about 40 wt % of the paraffin hydrocarbon wax, based upon the weight of the emulsion, about 0.01 to about 20 parts by weight of the saponifiable wax, per 100 parts of the paraffin wax, a saponifier, and about 0.1 to about 5 wt % of a dispersant, based upon the weight of the emulsion.
6. The process of claim 1 , wherein the concrete or cement formulation is prepared by admixing as an aqueous component a composition comprising a paraffin hydrocarbon wax, a saponifiable wax, a saponifier, and a dispersant.
7. The process of claim 1 , wherein the paraffin hydrocarbon wax has a melting point between about 50° C. to about 70° C., the saponifiable wax is a Montan wax having a melting point in the range of between about 70° C. to about 100° C., an acid number greater than 25, and a saponification number of greater than 85, the saponifier is ammonia hydroxide or an alkali metal hydroxide, and the dispersant is polynaphthalenesulfonic acid.