Method for producing a carbon fiber bundle
View Patent ↗A method to prepare a carbon fiber bundle which can develop satisfactory interfacial adhesion to polyolefin-based resins, especially polypropylene resins, is provided. The carbon fiber bundle comprises a plurality of single fibers sized with a sizing agent comprising: a polymer having a main chain formed of carbon-carbon bonds, containing an acid group in at least part of side chains or at least a part of main chain ends, and having an acid value of 23 to 120 mg KOH/g as measured in accordance with ASTM D1386; or a polymer having a main chain formed of carbon-carbon bonds and containing at least either of an epoxy group and an ester group in at least a part of side chains or at least a part of main chain ends.
1. A method for producing a carbon fiber bundle, comprising:
pre-sizing a carbon fiber bundle with an epoxy resin;
treating the pre-sized carbon fiber bundle with an aqueous sizing agent solution to obtain a sized wet carbon fiber bundle;
cutting the sized wet carbon fiber bundle to a prescribed length while regulating the moisture content of the pre-sized and treated carbon fiber bundle to 40 to 60 wt %; and
drying the carbon fiber bundle cut to the prescribed length,
wherein
the carbon fiber bundle which is to be treated comprises a plurality of single fibers, which comprise a plurality of wrinkles on their surface, wherein a vertical difference between a highest portion and a lowest portion in a region defined by 2 μm of circumferential length×1 μm of fiber axial direction length of the single fibers is 40 nm or more,
an amount of a sizing agent to the total weight is 1 to 5 wt %, and
the aqueous sizing agent solution is obtained by dissolving or dispersing in water, a sizing agent comprising:
a polymer having a main chain formed of carbon-carbon bonds which is selected from the group consisting of polypropylene, polyethylene and a copolymer of propylene and ethylene, comprising an acid group in at least a part of side chains or at least a part of main chain ends, wherein an acid value of the polymer comprising acid groups is 23 to 120 mg KOH/g as measured in accordance with ASTM D1386; and
an olefin-based thermoplastic elastomer resin having a Vicat softening point of 120° C. or less as measured according to ASTM D1525-70,
wherein
a weight ratio of the polymer having a main chain formed of carbon-carbon bonds to the olefin-based thermoplastic elastomer resin is from 15/1 to 1/1.