Atomic layer deposition coatings on razor components

1. A method for coating a razor blade comprising:

depositing, on at least one razor blade positioned in a vacuum chamber, at least one coating of at least one material, using an atomic layer deposition (ALD) process wherein said at least one coating covers an entire surface of at least one blade flank and at least a portion of a surface of a blade body of said at least one razor blade;

etching said at least one coating.

2. The method of claim 1 wherein said etching of said coating occurs on said at least one blade flank or on said blade body or on both said blade flank and said blade body.

3. The method of claim 1 wherein said etching removes said coating to produces a blade tip radius in the range of about 15 nm to about 40 nm.

4. The method of claim 1 wherein said etching occurs during said ALD process, after said ALD process, or both during and after said ALD process.

5. The method of claim 1 wherein said etching comprises directional, in-situ ion etching, chemical etching, RF etching, plasma, light-based etching or any combination thereof.

6. The method of claim 1 wherein said coating is conformal, has a substantially uniform thickness, smooth surface morphology and substantially zero porosity.

7. The method of claim 1 wherein said coating has a thickness ranging from about 0.1 nm to about 500 nm.

8. The method of claim 1 wherein said ALD process is applied for a time ranging from about 1 minute to about 10 hours and said etching is applied for a time ranging from about 2 minutes to about 1 hour.

9. The method of claim 1 wherein said razor blade is comprised of steel, Chromium (Cr), Diamond-like Carbon (DLC), Amorphous Diamond, Chromium/Platinum (Cr/Pt), Titanium, Titanium Nitride or Niobium or any combination thereof.

10. The method of claim 1 wherein said ALD process further comprises the steps of:

a. depositing a first monolayer of a first material onto said at least one razor blade;

b. depositing a second monolayer of a second material onto said at least one razor blade; and

c. repeating steps (a) and (b) until an optimal thickness of said at least one coating is produced.

11. The method of claim 10 wherein said first and second materials are the same.

12. The method of claim 10 wherein steps (a) or (b) further comprises the steps of:

d. evacuating said vacuum chamber;

e. introducing a first deposition precursor into said chamber to form an adsorbed layer on said at least one razor blade;

f. purging said vacuum chamber; and

g. introducing a second deposition precursor into said chamber to produce a monolayer of said material on said at least one razor blade.

13. The method of claim 12 where said first deposition precursor comprises Zirconium Chloride, Hafnium Chloride, Aluminum Chloride, or Titanium Chloride, or any combination thereof and said second deposition precursor comprises water vapor.

14. A method for coating a razor component comprising:

depositing, on at least one razor component, positioned in a vacuum chamber, at least one coating of at least one material using an ALD process.

15. The method of claim 14 wherein said razor component comprises a cartridge clip or at least a portion thereof, a blade support or at least a portion thereof, a razor blade body or at least a portion thereof, a razor blade flank or at least a portion thereof, a bent blade or at least a portion thereof, a razor handle or at least a portion thereof, or any combination thereof.

16. The method of claim 14 further comprises the step of etching said at least one coating.

17. The method of claim 14 wherein said coating has a thickness ranging from about 0.1 nm to about 2000 nm.