High performance gas turbine inlet filter (HEPA) using membrane media
View Patent ↗A composite filter media structure and an associated method of making are provided. The structure includes a base substrate that includes a nonwoven fabric substrate formed from a plurality of bicomponent synthetic fibers using a spunbond process. The composite filter media structure includes a surface layer deposited on one side of the base substrate where a thermal lamination process can be used to combine the base substrate and the surface layer. The surface layer is formed from a microporous expanded polytetrafluoroethylene membrane. In one aspect, the base substrate and the surface layer are configured to provide greater than 95% and equal to or less than 99.5% filtration efficiency measured in accordance with an EN 1822 test method. In another aspect, the filter media includes an embossing pattern or a plurality of corrugations formed using opposing rollers at a temperature of about 90° C. to about 140° C.
1. A composite filter media structure including:
a base substrate including a nonwoven fabric substrate formed from a plurality of bicomponent synthetic fibers using a spunbond process;
a surface layer deposited on one side of the base substrate wherein the surface layer is formed from a microporous expanded polytetrafluoroethylene membrane;
the base substrate and the surface layer are configured to provide greater than 95% and equal to or less than 99.5% filtration efficiency measured in accordance with an EN 1822 test method, and the composite filter media structure provides the greater than 95% and equal to or less than 99.5% fractional efficiency at pressure drops between approximately 0.60 inches of water and 3.05 inches of water.
2. A composite filter media structure according to claim 1 , wherein the surface layer has a basis weight of about 2.00 g/m 2 to about 3.50 g/m 2 .
3. A composite filter media structure according to claim 1 , wherein a thickness of the surface layer is approximately 5 to 25 microns.
4. A composite filter media structure according to claim 1 , wherein the composite filter media structure captures particle sizes of about 0.3 to about 1.25 microns.
5. A composite filter media structure according to claim 1 , wherein the composite filter media structure further including a plurality of corrugations.
6. A composite filter media structure according to claim 1 , wherein the air permeability of the composite filter media structure is between about 4.0 cubic feet per minute and about 10.0 cubic feet per minute at 0.5 inches of water pressure.
7. A gas turbine air inlet filter element including:
a first end cap;
a second end cap; and
a filter media, said filter media including:
a nonwoven synthetic fabric formed from a plurality of bicomponent synthetic fibers with a spunbond process;
a surface layer deposited on one side of the base substrate wherein the surface layer is formed from a microporous expanded polytetrafluoroethylene membrane;
wherein the base substrate and the surface layer are configured to provide greater than 95% and equal to or less than 99.5% filtration efficiency measured in accordance with an EN 1822 test method;
wherein said filter media further including an embossing pattern or a plurality of corrugations, said embossing pattern or said corrugations formed using opposing rollers at a temperature of about 90° C. to about 140° C.; and
the composite filter media structure provides the greater than 95% and equal to or less than 99.5% fractional efficiency at pressure drops between approximately 0.60 inches of water and 3.05 inches of water.
8. A composite filter media structure according to claim 7 , wherein the surface layer has a basis weight of about 2.00 g/m 2 to about 3.50 g/m 2 .
9. A composite filter media structure according to claim 7 , wherein a thickness of the surface layer is approximately 5 to 25 microns.
10. A filter element in accordance with claim 7 , wherein said plurality of corrugations include a plurality of alternating peaks and valleys extending a length of the composite filter media.
11. A filter element in accordance with claim 7 , wherein said composite filter media structure includes a corrugation pitch of about 3 to about 10 corrugations per inch and an effective depth of at least about 0.02 inch.
12. A method of making a composite filter media, the method including:
forming a nonwoven fabric substrate formed from a plurality of bicomponent synthetic fibers using a spunbond process; and
applying a surface layer of a microporous expanded polytetrafluoroethylene membrane on at least one side of the nonwoven fabric by thermal lamination to melt the synthetic fibers in to the surface layer to form the composite filter media such that the composite filter media has a filtration efficiency of greater than 95% and equal to or less than 99.5%, and the composite filter media structure provides the greater than 95% and equal to or less than 99.5% fractional efficiency at pressure drops between approximately 0.60 inches of water and 3.05 inches of water.
13. A method in accordance with claim 12 , wherein the step of applying the surface layer includes applying the surface layer with a basis weight of about 2.00 g/m 2 to about 3.50 g/m 2 .
14. A method in accordance with claim 12 , wherein the step of applying the surface layer includes applying the surface layer with a thickness of approximately 5 to 25 microns.
15. A method in accordance with claim 12 , wherein the air permeability of the surface layer before the thermal lamination is performed is between about 9.0 cubic feet per minute and about 12.0 cubic feet per minute at 0.5 inches of water pressure.
16. A method in accordance with claim 12 , wherein the composite filter media structure captures the most penetrating particle sizes of about 0.3 to about 1.25 microns.
17. A method in accordance with claim 12 , further including the step of corrugating the composite filter media structure.