Sizing Composition for Hot Penetrant Resistance
A process to increase the resistance of paper board to hot penetrants using a sizing agent containing fatty acid anhydride, and an insolubilizing agent is disclosed. Additionally a composition useful to impart hot penetrant resistance is disclosed
1 . A process to increase the resistance of paper board to penetration by hot penetrants, said process comprising a) adding i) an aqueous emulsion, comprising a reactive sizing agent and ii) an insolubilizing agent, either separately or in blended form to an aqueous pulp slurry, and wherein the reactive sizing agent comprises at least 30% fatty acid anhydride and b) forming the slurry into board or paperboard.
2 . The process of claim 1 wherein the paperboard is aseptic packaging board.
3 . The process of claim 1 wherein the pH of the pulp slurry is from about 6.5 to 7.5.
4 . The process of claim 1 wherein the pH of the pulp slurry is from about 6.7 to 7.3.
5 . The process of claim 1 wherein the reactive sizing agent comprises from 40 to 70% fatty acid anhydride.
6 . The process of claim 1 wherein the fatty acid anhydride is prepared from C14 to C22 linear saturated fatty acids.
7 . The process of claim 1 wherein the insolubilizing agent is selected from the group consisting of alum (aluminum sulfate), polyaluminum chloride (PAC) and other polyaluminum compounds.
8 . The process of claim 1 wherein the insolubilizing agent is alum.
9 . The process of claim 1 wherein the insolubilizing agent is added to the pulp slurry in an amount of from about 5 to about 15 lbs insolubilizing agent per ton of dry pulp.
10 . The process of claim 1 wherein the sizing agent further comprises an alkyl ketene dimer.
11 . The process of claim 10 wherein the alkyl ketene dimer is prepared from C14 to C22 linear saturated fatty acids.
12 . A process to increase the resistance of paper board to penetration by hot penetrants, said process comprising a) adding i) an aqueous emulsion, comprising a reactive sizing agent and ii) an insolubilizing agent, either separately or in blended form to an aqueous pulp slurry, wherein the pulp slurry is at a pH of 6.5 to 7.5, wherein the reactive sizing agent comprises at least 30% fatty acid anhydride and b) forming the slurry into aseptic packaging board.
13 . A composition which provides an improved resistance to hot hydrogen peroxide, the composition comprising a) fatty acid anhydride optionally comprising an alkyl ketene dimer, the weight ratio of the alkyl ketene dimer to fatty acid anhydride less than 2 to 1, and b) an insolubilizing agent.
14 . The composition of claim 13 wherein the insolubilizing agent is selected from the group consisting of alum (aluminum sulfate), polyaluminum chloride (PAC) and other polyaluminum compounds.
15 . The composition of claim 14 wherein the insolubilizing agent is alum.