Bioabsorbable polymeric composition for a medical device
View Patent ↗A biodegradable and biocompatible nontoxic polymeric composition is provided which includes a base material such as a crystallizable polymer, copolymer, or terpolymer, and a copolymer or terpolymer additive. Medical devices manufactured from the composition are also provided.
1. A method for making a bioabsorbable polymeric implant comprising the steps of:
blending a polymer composition comprising a crystallizable bioabsorbable polymer composition, wherein the crystallizable bioabsorbable polymer composition comprises at least about 70% (w/w) of a base polymer comprising a poly (L-lactide) moiety and/or poly (D-lactide) moiety, and/or poly L-lactide-co-PEG moiety, and/or poly D-lactide-co-PEG moiety, linked with a modifying copolymer thereof comprising poly (L-lactide-co-Tri-methylenecarbonate) and/or poly (D-lactide-co-Tri-methylene-carbonate) and/or poly (L-lactide-co-ε-caprolactone) and/or poly (D-lactide-co-ε-caprolactone) in the form of block copolymers or as blocky random copolymers; and
molding or extruding said polymer composition to produce a structurally tube configured implant wherein said polymer composition is crystallized.
2. The method according to claim 1 , wherein the polymer compositions affect a structural resilience by combining rigidity and flexibility characteristics to allow snap-fit interaction between suitable parts of the polymeric implant.
3. The method according to claim 1 , wherein the polymer composition forms a lactide racemate stereo complex crystal structure between the L-lactide and the D-lactide moieties.
4. The method according to claim 1 , wherein the polymer composition forms a lactide racemate stereo complex crystal structure, using the moieties comprising:
poly L-lactide with poly D-lactide with poly (L-lactide-co-tri-methylene-carbonate), or with poly (L-lactide-co-ε-caprolactone);
poly D-lactide with poly (L-lactide-co-tri-methylene-carbonate), or with poly (L-lactide-co-ε-caprolactone);
poly L-lactide with poly (D-lactide-co-tri-methylene-carbonate), or with poly (D-lactide-co-ε-caprolactone);
poly L-lactide with poly D-lactide with poly(D-lactide-co-tri-methylene-carbonate), or with poly (D-lactide-co-ε-caprolactone);
poly L-lactide-co-PEG with poly (D-lactide-co-tri-methylene-carbonate), or with poly (D-lactide-co-ε-caprolactone); and
poly D-lactide-co-PEG with poly (L-lactide-co-tri-methylene-carbonate), or with poly (L-lactide-co-ε-caprolactone).
5. The method of claim 1 , wherein the modifying copolymer is not more than about 40% of the composition.
6. The method of claim 1 , wherein a residual monomer concentration of the composition is less than 0.5%.
7. The method of claim 1 , further comprising the step of cutting said implant to form desired patterns.