Superconducting wire and manufacturing method thereof

1. A superconducting wire comprising:

a diffusion preventing tube having an outer circumferential surface in close contact with an inner circumferential surface of a stabilizing tube;

a plurality of modules collectively arranged within the diffusion preventing tube, the modules having a plurality of niobium filaments arranged at a copper matrix of a periphery of a tin rod positioned at a central part of a copper rod; and

a plurality of spacers inserted into inner spaces of the diffusion preventing tube,

wherein the superconducting wire is manufactured by collectively arranging the modules within the diffusion preventing tube, inserting the spacers into inner spaces of the diffusion preventing tube, and drawing the modules and the spacers, and

wherein one spacer is inserted into each space formed between the diffusion preventing tube and the modules as well as between the modules,

wherein a spacer inserted between the diffusion preventing tube and the modules or between three modules is either a tin/copper spacer having a tin or a tin alloy rod inserted into a central part of a copper or copper alloy rod or is a copper or copper alloy spacer, and

wherein a spacer inserted between four modules is a tin/copper spacer having a tin or tin alloy rod inserted into a central part of a copper or copper alloy rod.

2. A superconducting wire as claimed in claim 1 , wherein the tin/copper spacer inserted between the diffusion preventing tube and the modules as well as between the three modules has a sectional area rate of a copper or copper alloy rod respective to a tin or tin alloy rod, which is more than 6.0, based on a sectional surface perpendicular to an axial direction, and a tin/copper spacer inserted between the four modules has a sectional area rate of a copper or copper alloy rod respective to a tin or tin alloy rod, which is less than substantially 0.01-6.0, based on a sectional surface perpendicular to an axial direction.

3. A superconducting wire as claimed in claim 1 , wherein a number of the modules is 19, 37, or 64.

4. A superconducting wire as claimed in claim 1 , wherein an entire sectional rate of tin rods positioned at central parts of the modules and tin rods positioned at central parts of spacers, respective to an entire sectional area of niobium filaments and copper of the modules positioned within the diffusion preventing tube, is within a range of substantially 10-40%.

5. A method for manufacturing a superconducting wire, comprising the steps of:

extruding an extrusion billet having niobium filaments inserted into an interior of a copper rod in an axial direction so as to manufacture an extrusion rod material;

boring a hole through a central part of the extrusion rod material, inserting one of a tin rod or a tin alloy rod into the hole, and performing a drawing process so as to manufacture a subelement;

collectively arranging a plurality of modules at an interior of the diffusion preventing tube, the modules being formed by cutting the subelement into a proper length and cleaning the subelement; and

manufacturing a restacking billet by inserting a spacer into each inner space within the diffusion preventing tube,

wherein the step of manufacturing the restacking billet comprises the steps of:

dividing inner spaces formed by the diffusion preventing tube and the modules into a triangular space formed between three modules, a square space formed between four modules, and an outer space formed between the diffusion preventing tube and two modules;

inserting either a tin/copper spacer or inserting a copper or copper alloy spacer into the triangular space and the outer space, the tin/copper spacer having a tin or tin alloy rod inserted into a central part of a copper or copper alloy rod; and

inserting a tin/copper spacer into the square space, the tin/copper spacer having a tin or tin alloy rod inserted into a central part of a copper or copper alloy rod.

6. The method for manufacturing a superconducting wire as claimed in claim 5 , wherein a sectional area rate of the copper or copper alloy rod respective to the tin or tin alloy rod of the tin/copper spacer inserted into the triangular space and the outer space is higher, based on a sectional surface perpendicularly to an axial direction, than a sectional area rate of the copper or copper alloy rod respective to the tin or tin alloy rod of the tin/copper spacer inserted between the four modules.