BIO-BASED CARPET MATERIALS
The present invention disclosures the use of castor oil and castor oil derivatives for use in polyurethane formulations for the production of products for the carpet industry. Process for the production of such products is also disclosed.
1 . A process for preparing a foam backed textile, an unattached padding or underlay comprising the steps of
A) forming a polyurethane-forming composition comprising
i) a polyisocyanate
ii) a polyol,
iii) from 0.0 to 4 weight percent water based on weight of polyol;
iv) from 0.5 to 2.5 weight percent surfactant based on weight of polyol);
B) mechanically frothing the polyurethane-forming composition;
C) applying the frothed composition of step B) to a substrate or release capable belt;
D) heating the composition to a temperature from 80 to 180° C. to cure the composition and form a polyurethane layer bonded to the substrate;
wherein the polyol comprises from 5 to 60 weight percent of castor oil, castor oil derivative, or a combination thereof and the remaining polyol is a polyol or polyol blend having a nominal functionality of 2 to 3 and a hydroxyl number of 5.6 to 70.
2 . The process of claim 1 wherein the substrate is a polymeric film, a polymer sheet, carpet, textile fabric or artificial turf.
3 . The process of claim 1 wherein the isocyanate is an isocyanate terminated prepolymer.
4 . The process of claim 1 wherein the amount of castor oil or castor oil derivative is at least 10 weight percent of the polyol.
5 . The process of claim 4 wherein the castor oil or castor oil derivatives comprises at least 15 weight percent of the polyol.
6 . A process for preparing a carpet material comprising providing tufts, a primary backing material, and a pre-coat
engaging the tufts and the primary backing thereby forming greige goods having a top and bottom surface;
applying the pre-coat onto the bottom surface of the greige goods; and optionally curing the pre-coat,
wherein the precoat/laminate or tie-/tie-coating comprises
a) a polyisocyanate and
b) a polyol wherein the polyols comprises from 5 to 80 weight percent of a modified castor oil having a nominal functionality of 1.8 to 2.5 and the remainder of the polyol is a polyol or polyol blend having a nominal functional of 1.8 to 2.5 and a hydroxyl number of 5.6 to 70.
7 . The process of claim 6 wherein the isocyanate is an isocyanate terminated prepolymer.
8 . The process of claim 7 wherein the castor oil or castor oil derivative comprises at least 10 weight percent of the polyol.
9 . The process of claim 8 wherein the castor oil or castor oil derivative comprises at least 15 weight percent of the polyol.
10 . A process comprising
a) forming a frothed polyurethane-forming composition;
b) forming a layer of frothed composition between a substrate and a containment layer;
c) curing the frothed composition to form a foamed polyurethane cushion bonded to
the substrate or to both the substrate and containment layer; wherein the frothed polyurethane forming composition comprises
i) a polyisocyanate
ii) a polyol,
iii) from 0.0 to 4 weight percent water based on weight of polyol;
iv) from 0.5 to 2.5 weight percent surfactant based on weight of polyol;
wherein the polyol comprises from 5 to 60 weight percent of castor oil, castor oil derivative, or a combination thereof and the remaining polyol is a polyol or polyol blend having a nominal functionality of 2 to 3 and a hydroxyl number of 5.6 to 70.
11 . The process of claim 10 wherein the substrate is a polymeric film, a polymer sheet, carpet, textile fabric or artificial turf.
12 . The process of claim 10 wherein the isocyanate is an isocyanate terminated prepolymer.
13 . The process of claim 1 wherein the amount of castor oil or castor oil derivative is at least 10 weight percent of the polyol.
14 . The process of claim 13 wherein the castor oil or castor oil derivatives comprises at least 15 weight percent of the polyol.
15 . An article made by the process of claims 10 .