THERMALLY STABLE THERMOPLASTIC VULCANIZATE COMPOUNDS
A high temperature thermoplastic vulcanizate is disclosed, which achieves its long term heat aging performance from a set of heat stabilizers, at least one of which stabilizes the thermoplastic phase and at least one of which stabilizes the elastomeric phase. Plastic articles made from the high temperature thermoplastic vulcanizate are also disclosed. The thermoplastic vulcanizate can be made by melt mixing or by dynamic vulcanization in an extruder.
1 . A high temperature thermoplastic vulcanizate, comprising:
(a) a thermoplastic phase,
(b) an elastomeric phase, and
(c) a set of heat stabilizers at least one of which stabilizes the thermoplastic phase and at least one of which stabilizes the elastomeric phase.
2 . The thermoplastic vulcanizate of claim 1 , wherein the thermoplastic phase is continuous and the elastomeric phase is discontinuous.
3 . The thermoplastic vulcanizate of claim 1 , wherein the thermoplastic phase is a polymer selected from the group consisting of homopolymers and copolymers of lower α-olefins.
4 . The thermoplastic vulcanizate of claim 1 , wherein the elastomeric phase is a polymer selected from the group consisting of natural rubber, polyisoprene rubber, styrenic copolymer elastomers, polybutadiene rubber, nitrile rubber, butyl rubber, and olefinic elastomer, and combinations thereof.
5 . The thermoplastic vulcanizate of claim 1 , wherein the thermoplastic phase stabilizer is selected from the group consisting of phenolics, phosphites, thioesters, and combinations thereof.
6 . The thermoplastic vulcanizate of claim 1 , wherein the elastomeric phase stabilizer is selected from the group consisting of metal chelators, aromatic amines, and combinations thereof.
7 . The thermoplastic vulcanizate of claim 1 , further comprising a vulcanizate crosslinker and wherein the thermoplastic vulcanizate is dynamically vulcanized.
8 . The thermoplastic vulcanizate of claim 1 , further comprising optional additives selected from the group consisting of adhesion promoters; biocides (antibacterials, fungicides, and mildewcides), anti-fogging agents; anti-static agents; bonding, blowing and foaming agents; dispersants; fillers and extenders; fire and flame retardants and smoke suppressants; impact modifiers; initiators; lubricants; micas; pigments, colorants and dyes; plasticizers; processing aids; release agents; silanes, titanates and zirconates; slip and anti-blocking agents; stabilizers other than those already mentioned; stearates; ultraviolet light absorbers; viscosity regulators; waxes; and combinations of them.
9 . The thermoplastic vulcanizate of claim 1 ,
wherein the amount of thermoplastic phase ranges from about 10 to about 70 weight percent of the thermoplastic vulcanizate;
wherein the amount of elastomeric phase ranges from about 20 to about 90 weight percent of the thermoplastic vulcanizate; and
wherein the amount of the set of stabilizers ranges from about 0.1 to about 1 weight percent of the thermoplastic vulcanizate.
10 . A plastic article made from the thermoplastic vulcanizate of claim 1 .
11 . The plastic article of claim 10 , wherein the thermoplastic phase is continuous and the elastomeric phase is discontinuous.
12 . The plastic article of claim 10 , wherein the thermoplastic phase is a polymer selected from the group consisting of homopolymers and copolymers of lower α-olefins.
13 . The plastic article of claim 10 , wherein the elastomeric phase is a polymer selected from the group consisting of natural rubber, polyisoprene rubber, styrenic copolymer elastomers, polybutadiene rubber, nitrile rubber, butyl rubber, and olefinic elastomer, and combinations thereof.
14 . The plastic article of claim 10 , wherein the thermoplastic phase stabilizer is selected from the group consisting of phenolics, phosphites, thioesters, and combinations thereof.
15 . The plastic article of claim 10 , wherein the elastomeric phase stabilizer is selected from the group consisting of metal chelators, aromatic amines, and combinations thereof.
16 . The plastic article of claim 10 , wherein the thermoplastic vulcanizate further comprises a vulcanizate crosslinker and wherein the thermoplastic vulcanizate is dynamically vulcanized.
17 . The plastic article of claim 10 , wherein the thermoplastic vulcanizate further comprises optional additives selected from the group consisting of adhesion promoters; biocides (antibacterials, fungicides, and mildewcides), anti-fogging agents; anti-static agents; bonding, blowing and foaming agents; dispersants; fillers and extenders; fire and flame retardants and smoke suppressants; impact modifiers; initiators; lubricants; micas; pigments, colorants and dyes; plasticizers; processing aids; release agents; silanes, titanates and zirconates; slip and anti-blocking agents; stabilizers other than those already mentioned; stearates; ultraviolet light absorbers; viscosity regulators; waxes; and combinations of them.
18 . The plastic article of claim 10 ,
wherein the amount of thermoplastic phase ranges from about 10 to about 70 weight percent of the thermoplastic vulcanizate;
wherein the amount of elastomeric phase ranges from about 20 to about 90 weight percent of the thermoplastic vulcanizate; and
wherein the amount of the set of stabilizers ranges from about 0.1 to about 1 weight percent of the thermoplastic vulcanizate.