Crosslinkable polyethylene composition, method of making the same, and articles made therefrom
View Patent ↗The instant invention is a crosslinkable polyethylene composition obtained via a process comprising the steps of (1) providing a polyethylene component; (2) providing an organic peroxide crosslinking agent,(3) providing a crosslinking coagent which comprises at least two terminal carbon-carbon double bonds and is an alkadiene, alkatriene, or alkatetraene compound; (4) melt blending the polyethylene component, the crosslinking agent, and the crosslinking coagent at a temperature less than the decomposition temperature of the crosslinking agent; and (5) thereby forming the crosslinkable polyethylene composition. The crosslinkable polyethylene composition may further include a scorch inhibitor, a cure booster, a stable free radical, one or more conventional additives, and/or combinations thereof. The instant invention further includes articles comprising the crosslinked product of the crosslinkable polyethylene composition.
1. A method for crosslinking a crosslinkable polyethylene composition comprising the steps of:
providing a polyethylene component;
providing a crosslinking agent, wherein said crosslinking agent being an organic peroxide;
providing a crosslinking coagent, wherein said crosslinking coagent being a alkadiene, alkatriene, or alkatetraene compound, wherein said crosslinking coagent comprises at least two terminal carbon-carbon double bonds;
melt blending said polyethylene component, said crosslinking agent, and said crosslinking agent;
thereby forming said crosslinkable polyethylene composition;
subjecting said crosslinkable polyethylene composition to heat thereby raising the temperature of said crosslinkable polyethylene composition to a temperature in the range of greater than the decomposition temperature of said crosslinking agent;
thereby crosslinking said crosslinkable polyethylene composition and forming a crosslinked polyethylene composition,
wherein said crosslinked polyethylene composition has a gel content in the range of from 83 to 90 weight percent based on the entire weight of said crosslinked polyethylene composition.
2. An article comprising at least one component formed from the crosslinked product of:
a polyethylene component;
a crosslinking agent, wherein said crosslinking agent being an organic peroxide; and
a crosslinking coagent, wherein said crosslinking coagent being an alkadiene, alkatriene, or alkatetraene compound, wherein said crosslinking coagent comprises at least two terminal carbon-carbon double bonds,
wherein said crosslinked product has a gel content in the range of from 83to 90 weight percent based on the entire weight of said crosslinked product.
3. A method for producing an article comprising the steps of:
providing a polyethylene component;
providing a crosslinking agent, wherein said crosslinking agent being an organic peroxide;
providing a crosslinking coagent, wherein said crosslinking coagent being an alkadiene, alkatriene, or alkatetraene compound, wherein said crosslinking coagent comprises at least two terminal carbon-carbon double bonds;
melt blending said polyethylene component, said crosslinking agent, and said crosslinking agent;
thereby forming a crosslinkable polyethylene composition;
shaping said crosslinkable polyethylene composition;
subjecting said shaped crosslinkable polyethylene composition to heat thereby raising the temperature of said shaped crosslinkable polyethylene composition to a temperature in the range of greater than the decomposition temperature of said crosslinking agent;
thereby crosslinking said shaped crosslinkable polyethylene composition and forming a shaped crosslinked polyethylene composition;
thereby forming said article,
wherein said shaped crosslinked polyethylene composition has a gel content in the range of from 83 to 90 weight percent based on the entire weight of said shaped crosslinked polyethylene composition.