Manufacturing method of hexafluorophosphate
View Patent ↗In the manufacturing method of hexafluorophosphate (MPF 6 : M=Li, Na, K, Rb, Cs, NH 4 , and Ag) of the present invention, at least a H x PO y F z aqueous solution, a hydrofluoric acid aqueous solution, and MF.r (HF) are used as raw materials (wherein, r≧0, 0≦x≦3, 0≦y≦4, and 0≦z≦6). According to the above description, a manufacturing method of hexafluorophosphate can be provided which is capable of manufacturing hexafluorophosphate (GPF 6 : G=Li, Na, K, Rb, Cs, NH 4 , and Ag) at a low cost in which the raw materials can be easily obtained, the control of the reaction is possible, and the workability is excellent.
1. A manufacturing method of hexafluorophosphate (MPF 6 : M is at least one kind selected from the group consisting of Li, Na, K, Rb, Cs, NH 4 , and Ag) comprising steps of:
providing at least a H x PO y F z aqueous solution, a hydrofluoric acid aqueous solution, and MF.r (HF) as raw materials, wherein, r≧0, 0≦x≦3, 0≦y≦4, and 0≦z≦6; and
producing the hexafluorophosphate from the raw materials.
2. The manufacturing method of hexafluorophosphate according to claim 1 , wherein MPF 6 is synthesized by reacting the H x PO y F z aqueous solution with the hydrofluoric acid aqueous solution according to Formula 1, extracting a crystal of a hexafluorophosphoric acid hydrate (HPF 6 .qH 2 O) as a solid once, and then reacting the extracted HPF 6 .qH 2 O with MF.r (HF) according to Formula 2,
H x PO y F z +pHF→HPF 6 .qH 2 O (Formula 1)
(wherein, p>0,p+z>6, and q≧1)
HPF 6 .qH 2 O+MF.r (HF)→MPF 6 +(r+1)HF+qH 2 O (Formula 2).
3. The manufacturing method of hexafluorophosphate according to claim 1 , wherein MPF 6 is synthesized by reacting the H x PO y F z aqueous solution, the hydrofluoric acid aqueous solution, and MF.r(HF) all at once according to Formula 3,
MF.r (HF)+H x PO y F z +sHF→MPF 6 +yH 2 O (Formula 3)
(wherein, s is 1 or more, and 0<y≦4).
4. The manufacturing method of hexafluorophosphate according to claim 1 , wherein the H x PO y F Z has a concentration of 50 to 98% by weight in the H x PO y F z aqueous solution.
5. The manufacturing method of hexafluorophosphate according to claim 1 , wherein the H xl PO y F z has a concentration of 75% by weight to 85% by weight in the H x PO y F z aqueous solution.
6. The manufacturing method of hexafluorophosphate according to claim 1 , wherein the hydrofluoric acid in the hydrofluoric acid aqueous solution used has a concentration of 40% by weight or more.
7. The manufacturing method of hexafluorophosphate according to claim 1 , wherein the hydrofluoric acid in the hydrofluoric acid aqueous solution used has a concentration of 50% by weight to 75% by weight.
8. The manufacturing method of hexafluorophosphate according to claim 1 , wherein the concentration of the hydrofluoric acid in the hydrofluoric acid aqueous solution after reacting at least two out of: the H x PO y F z aqueous solution; the HF aqueous solution; and MF.r (HF) is kept at 40% by weight or more.
9. The manufacturing method of hexafluorophosphate according to claim 8 , wherein the concentration of the hydrofluoric acid in the hydrofluoric acid aqueous solution after reacting at least two out of: the H x PO y F z aqueous solution; the HF aqueous solution; and MF.r (HF) is kept at 45% by weight or more and less than 65% by weight.
10. The manufacturing method of hexafluorophosphate according to claim 1 , wherein in the producing step, HPF 6 .qH 2 O is crystallized by reacting the H x PO y F z aqueous solution and the hydrofluoric acid aqueous solution.
11. The manufacturing method of hexafluorophosphate according to claim 10 , wherein the crystallization is performed at −50° C. or more to 0° C. or less.