Dental composition
View Patent ↗A composition for dental use containing a polymerizable monomer (a) having an aromatic ring and a hydroxyl group, a polymerizable monomer (b) having an aromatic ring without having any hydroxyl groups, and a polymerizable monomer (c) other than the polymerizable monomers (a) and (b), wherein the composition for dental use contains the polymerizable monomers (a), (b), and (c) in an amount of from 10 to 30% by weight, from 50 to 70% by weight, and from 10 to 30% by weight, respectively, of all the polymerizable monomers. The composition for dental use of the present invention can be suitably used as a product capable of substituting a part or all of a natural tooth in the field of dental therapy.
1. A composition, comprising:
a polymerizable monomer (a) comprising an aromatic ring and a hydroxyl group;
a polymerizable monomer (b) comprising an aromatic ring and no hydroxyl groups;
a polymerizable monomer (c) other than the polymerizable monomers (a) and (b); and
alumina particles (d),
wherein the composition comprises the polymerizable monomers (a), (b), and (c) in an amount of from 10 to 30% by weight, from 50 to 70% by weight, and from 10 to 30% by weight, respectively, of all the polymerizable monomers,
wherein the alumina particles (d) satisfy requirements (i) and (ii):
(i) a refractive index (n A ) is from 1.60 to 1.70; and
(ii) a proportion of particles having particle sizes of from 0.005 to 0.1 μm is 95% by number or more, and
wherein a ratio of WA, a weight of the alumina particles (d), and WM, a total weight of the polymerizable monomers (a), (b), and (c), WA/WM, is from 1.5 to 2.5.
2. The composition of claim 1 , wherein the polymerizable monomer (a) is a compound comprising a bisphenol A backbone and a hydroxyl group, and wherein the polymerizable monomer (b) is a compound comprising a bisphenol A backbone and no hydroxyl groups.
3. The composition of claim 1 , further comprising inorganic particles (e) other than the alumina particles (d), wherein the inorganic particles (e) satisfy requirements (iii), (iv), and (v):
(iii) a refractive index (n F ) is from 1.50 to 1.65;
(iv) a proportion of particles having particle sizes of from 0.01 to 100 μm is 95% by volume or more; and
(v) a volume-median particle size is from 0.1 to 20 μm.
4. The composition of claim 3 , wherein WM, a total weight of the polymerizable monomers (a), (b), and (c), WA, a weight of the alumina particles (d), and WF, a weight of the inorganic particles (e) satisfy:
[( WF+WA )/( WM+WA+WF )]×100≧80.
5. The composition of claim 2 , further comprising inorganic particles (e) other than the alumina particles (d), wherein the inorganic particles (e) satisfy requirements (iii), (iv), and (v):
(iii) a refractive index (n F ) is from 1.50 to 1.65;
(iv) a proportion of particles having particle sizes of from 0.01 to 100 μm is 95% by volume or more; and
(v) a volume-median particle size is from 0.1 to 20 μm.
6. The composition of claim 5 , wherein WM, a total weight of the polymerizable monomers (a), (b), and (c), WA, a weight of the alumina particles (d), and WF, a weight of the inorganic particles (e) satisfy:
[( WF+WA )/( WM+WA+WF )]×100≧80.
7. A method of substituting a part or all of a natural tooth, the method comprising:
(A) filling a cavity of a natural tooth with a composition comprising
at least one polymerizable monomer (a) comprising an aromatic ring and a hydroxyl group,
at least one polymerizable monomer (b) comprising an aromatic ring and no hydroxyl groups,
at least one polymerizable monomer (c) other than the polymerizable monomers (a) and (b), and
alumina particles (d),
wherein the composition comprises the polymerizable monomers (a), (b), and (c) in an amount of from 10 to 30% by weight, from 50 to 70% by weight, and from 10 to 30% by weight, respectively, of all the polymerizable monomers
wherein the alumina particles (d) satisfy requirements (i) and (ii):
(i) a refractive index (n A ) is from 1.60 to 1.70; and
(ii) a proportion of particles having particle sizes of from 0.005 to 0.1 μm is 95% by number or more, and
wherein a ratio of WA, a weight of the alumina particles (d), and WM, a total weight of the polymerizable monomers (a), (b), and (c), WA/WM, is from 1.5 to 2.5; and
(B) curing the composition.
8. A method of preparing a composition operable for substituting a part or all of a natural tooth, the method comprising:
(A) mixing components comprising
at least one polymerizable monomer (a) comprising an aromatic ring and a hydroxyl group,
at least one polymerizable monomer (b) comprising an aromatic ring and no hydroxyl groups,
at least one polymerizable monomer (c) other than the polymerizable monomers (a) and (b), and
alumina particles (d), to obtain the composition,
wherein the composition comprises the polymerizable monomers (a), (b), and (c) in an amount of from 10 to 30% by weight, from 50 to 70% by weight, and from 10 to 30% by weight, respectively, of all the polymerizable monomers,
wherein the alumina particles (d) satisfy requirements (i) and (ii):
(i) a refractive index (n A ) is from 1.60 to 1.70; and
(ii) a proportion of particles having particle sizes of from 0.005 to 0.1 μm is 95% by number or more, and
wherein a ratio of WA, a weight of the alumina particles (d), and WM, a total weight of the polymerizable monomers (a), (b), and (c), WA/WM, is from 1.5 to 2.5.
9. The composition of claim 1 , wherein the composition is suitable for substituting a part or all of a natural tooth.