Quality polymer foam from fluorinated alkene blowing agents
View Patent ↗Alkenyl aromatic polymer foam comprising a polymer matrix containing one or more polymer and defining a plurality of cells having an average cell size wherein: (a) the alkenyl aromatic polymer foam has: —(i) an average cell size that is in a range of 0.02 and 5 millimeters; —(ii) a density of 64 kilograms per cubic meter or less; —(iii) an open cell content less than 30 percent; and —(iv) a cell size variation of 30% or less; and wherein the foam further comprises one or more fluorinated alkene blowing agent at a concentration of 0.03 moles or more and 0.3 moles or less per 100 grams of polymer foam.
1. An alkenyl aromatic polymer foam comprising a polymer matrix containing one or more polymer and defining a plurality of cells having an average cell size wherein:
(a) the alkenyl aromatic polymer foam has:
(i) an average cell size according to ASTM method D-3576-04 that is in a range of 0.02 and 5 millimeters;
(ii) a density of 64 kilograms per cubic meter or less according to ISO method 845-85;
(iii) an open cell content less than 30 percent according to ASTM method D6226-05; and
(iv) a cell size variation of 30% or less; and
(b) 50 weight-percent or more of the one or more polymer consists of one or more polymer selected from a group consisting of alkenyl aromatic polymers; and
wherein the alkenyl aromatic polymer foam further comprises one or more fluorinated alkene blowing agent at a concentration of 0.03 moles or more and 0.3 moles or less per 100 grams of polymer foam, the one or more fluorinated alkene blowing agent being selected from a group consisting of: hexafluoropropene; 2-fluoropropene, 1-fluoropropene; 1,1-difluoropropene; 3,3-difluoropropene; 3,3,3-trifluoropropene; 2,3,3-trifluoropropene; 1,3,3,3-tetrafluoropropene; 1,1,3,3-tetrafluoropropene; 1,2,3,3,3-pentafluoropropene; 4,4,4-trifluoro-1-butene; 3,4,4,4-tetrafluoro-1-butene; 1,1,3,3,3-pentafluoro-2-methyl-1-propene; octafluoro-1-butene; octafluoro-2-butene; 2,3,3,4,4,4-hexafluoro-1-butene; 1,1,1,4,4,4-hexafluoro-2-butene; 1,1,1,2,4,4,4-heptafluoro-2-butene; 3-fluoropropene, 2,3-difluoropropene; 1,1,3-trifluoropropene; 1,3,3-trifluoropropene; 1,1,2-trifluoropropene; 1-fluorobutene; 2-fluorobutene; 2-fluoro-2-butene; 1,1-difluoro-1-butene; 3,3-difluoro-1-butene; 3,4,4-trifluoro-1-butene; 2,3,3-trifluoro-1-butene; 1,1,3,3-tetrafluoro-1-butene; 1,4,4,4-tetrafluoro-1-butene; 3,3,4,4-tetrafluoro-1-butene; 4,4-difluoro-1-butene; 1,1,1-trifluoro-2-butene; 2,4,4,4-tetrafluoro-1-butene; 1,1,1,2-tetrafluoro-2 butene; 1,1,4,4,4-pentafluoro-1-butene; 2,3,3,4,4-Pentafluoro-1-butene; 1,2,3,3,4,4,4-Heptafluoro-1-butene; 1,1,2,3,4,4,4-Heptafluoro-1-butene; and 1,3,3,3-tetrafluoro-2-(trifluoromethyl)-Propene.
2. The alkenyl aromatic polymer foam of claim 1 , wherein the polymer foam is essentially free of blowholes.
3. The alkenyl aromatic polymer foam of claim 1 , wherein the one or more fluorinated alkene is selected from a group consisting of 3-fluoropropene, 2,3-difluoropropene; 1,1,3-trifluoropropene; 1,3,3-trifluoropropene; 1,1,2-trifluoropropene; 1-fluorobutene; 2-fluorobutene; 2-fluoro-2-butene; 1,1-difluoro-1-butene; 3,3-difluoro-1-butene; 3,4,4-trifluoro-1-butene; 2,3,3-trifluoro-1-butene; 1,1,3,3-tetrafluoro-1-butene; 1,4,4,4-tetrafluoro-1-butene; 3,3,4,4-tetrafluoro-1-butene; 4,4-difluoro-1-butene; 1,1,1-trifluoro-2-butene; 2,4,4,4-tetrafluoro-1-butene; 1,1,1,2-tetrafluoro-2 butene; 1,1,4,4,4-pentafluoro-1-butene; 2,3,3,4,4-Pentafluoro-1-butene; 1,2,3,3,4,4,4-Heptafluoro-1-butene; 1,1,2,3,4,4,4-Heptafluoro-1-butene; and 1,3,3,3-tetrafluoro-2-(trifluoromethyl)-Propene.
4. The alkenyl aromatic polymer foam of claim 1 , wherein the one or more fluorinated alkene is the only blowing agent in the alkenyl aromatic polymer foam.
5. The alkenyl aromatic polymer foam of claim 1 , wherein the alkenyl aromatic polymer is one or more polymer selected from polystyrene polymers and styrene-acrylonitrile copolymers.
6. The alkenyl aromatic polymer foam of claim 1 , wherein the foam has a thickness that is nine millimeters or more.
7. A process for preparing an alkenyl aromatic polymer foam comprising the following steps in order:
(a) providing a foamable composition comprising a polymer and a blowing agent, wherein more than 50 weight-percent of the polymer consists of one or more alkenyl aromatic polymer; and
(b) expanding the foamable composition into a polymer foam of claim 1 ,
wherein the blowing agent comprises one or more fluorinated alkene at a concentration of 0.03 moles or more and 0.3 moles or less per 100 grams of polymer, the fluorinated alkene being selected from a group consisting of: hexafluoropropene; 2-fluoropropene, 1-fluoropropene; 1,1-difluoropropene; 3,3-difluoropropene; 3,3,3-trifluoropropene; 2,3,3-trifluoropropene; 1,3,3,3-tetrafluoropropene; 1,1,3,3-tetrafluoropropene; 1,2,3,3,3-pentafluoropropene; 4,4,4-trifluoro-1-butene; 3,4,4,4-tetrafluoro-1-butene; 1,1,3,3,3-pentafluoro-2-methyl-1-propene; octafluoro-1-butene; octafluoro-2-butene; 2,3,3,4,4,4-hexafluoro-1-butene; 1,1,1,4,4,4-hexafluoro-2-butene; 1,1,1,2,4,4,4-heptafluoro-2-butene; 3-fluoropropene, 2,3-difluoropropene; 1,1,3-trifluoropropene; 1,3,3-trifluoropropene; 1,1,2-trifluoropropene; 1-fluorobutene; 2-fluorobutene; 2-fluoro-2-butene; 1,1-difluoro-1-butene; 3,3-difluoro-1-butene; 3,4,4-trifluoro-1-butene; 2,3,3-trifluoro-1-butene; 1,1,3,3-tetrafluoro-1-butene; 1,4,4,4-tetrafluoro-1-butene; 3,3,4,4-tetrafluoro-1-butene; 4,4-difluoro-1-butene; 1,1,1-trifluoro-2-butene; 2,4,4,4-tetrafluoro-1-butene; 1,1,1,2-tetrafluoro-2 butene; 1,1,4,4,4-pentafluoro-1-butene; 2,3,3,4,4-Pentafluoro-1-butene; 1,2,3,3,4,4,4-Heptafluoro-1-butene; 1,1,2,3,4,4,4-Heptafluoro-1-butene; and 1,3,3,3-tetrafluoro-2-(trifluoromethyl)-Propene.
8. The process of claim 7 , wherein more than 50 weight-percent of the blowing agent consists of one or more of the fluorinated alkenes.
9. The process of claim 7 , wherein the blowing agent further comprises one or more blowing agent selected from a group consisting of fluorinated alkanes having from one to five carbons, hydrocarbons having from one to nine carbons, alcohols having from one to two to five carbons, water and carbon dioxide.
10. The process of claim 7 , wherein the blowing agent consists of the one or more fluorinated alkene and one or more blowing agent selected from carbon dioxide and water.
11. The process of claim 7 , wherein the one or more fluorinated alkene is selected from a group consisting of 3-fluoropropene, 2,3-difluoropropene; 1,1,3-trifluoropropene; 1,3,3-trifluoropropene; 1,1,2-trifluoropropene; 1-fluorobutene; 2-fluorobutene; 2-fluoro-2-butene; 1,1-difluoro-1-butene; 3,3-difluoro-1-butene; 3,4,4-trifluoro-1-butene; 2,3,3-trifluoro-1-butene; 1,1,3,3-tetrafluoro-1-butene; 1,4,4,4-tetrafluoro-1-butene; 3,3,4,4-tetrafluoro-1-butene; 4,4-difluoro-1-butene; 1,1,1-trifluoro-2-butene; 2,4,4,4-tetrafluoro-1-butene; 1,1,1,2-tetrafluoro-2 butene; 1,1,4,4,4-pentafluoro-1-butene; 2,3,3,4,4-Pentafluoro-1-butene; 1,2,3,3,4,4,4-Heptafluoro-1-butene; 1,1,2,3,4,4,4-Heptafluoro-1-butene; and 1,3,3,3-tetrafluoro-2-(trifluoromethyl)-Propene.
12. The process of claim 11 , wherein the blowing agent consists of the one or more fluorinated alkene.
13. The process of claim 7 , wherein the alkenyl aromatic polymer is one or more polymer selected from polystyrene polymers, styrene-acrylonitrile copolymer and blends thereof.
14. The process of claim 7 , wherein the one or more alkenyl aromatic polymer comprises 95 weight-percent or more of the polymer in the foamable composition.
15. The process of claim 7 , wherein the process is an extrusion process where step (a) includes softening the polymer in an extruder, mixing the blowing agent into the softened polymer at an addition temperature and addition pressure to form the foamable composition and then cooling the foamable composition to a foaming temperature and step (b) includes expelling the foamable composition through a die at the foaming temperature into an environment at a lower pressure than the mixing pressure.
16. The process of claim 7 , wherein the process is an expanded bead foam process where the foamable composition in step (a) is in the form of beads and step (b) includes steam expanding the polymer beads.
17. The process of claim 7 , wherein step (b) requires expanding the foamable composition into a polymer foam having a thickness of nine millimeters or more.
18. A method of using the alkenyl aromatic polymer foam of claim 1 comprising the step of positioning the polymer foam between two areas where one of the two areas experiences a different temperature than the other area.