Method of repair
View Patent ↗Provided is a method of repair which method is capable of holding a molten brazing material at the bonding portion when a component is bonded with a brazing material to an inclined or to a curved surface. The method of repair repairs by brazing a repair portion in which a crack has developed and which needs repair, wherein a brazing material support ( 4 ) holding in the interior thereof a molten brazing material ( 5 ) is brought into contact with the repair portion, and under the condition that the brazing material support ( 4 ) is in contact with the repair portion, the molten brazing material ( 5 ) is solidified. Under the condition that the brazing material ( 5 ) in a powder form is brought into contact with the brazing material support ( 4 ), the brazing material ( 5 ) can be melted by heating to a temperature at or above the melting point of the brazing material ( 5 ). Alternatively, under the condition that the brazing material support ( 4 ) in the interior of which the brazing material ( 5 ) has been beforehand held is brought into contact with the repair portion, the brazing material ( 5 ) can be melted by heating to a temperature at or above the melting point of the brazing material ( 5 ).
1. A method of repair, said method comprising:
brazing a repair portion of a base, wherein the repair portion needs to be repaired;
placing a brazing material support in the interior of the base; and
providing a brazing material in contact with the repair portion,
wherein
when the brazing material support is in contact with the repair portion, the brazing material is solidified,
the brazing material support is a porous material having a three-dimensional network structure in which pores of the porous material are communicatively connected to each other,
the brazing material support comprises at least one of metal wool, metal nonwoven fabric or metal gauze,
the brazing material support is made of a material equivalent to the base, and
heating the brazing material to a temperature at or above the melting point of the brazing material when the brazing material in a powder form is brought into contact with the brazing material support, so that the brazing material is melted.
2. The method of repair according to claim 1 , further comprising heating the brazing material in a powder form to a temperature at or above the melting point of the brazing material after the brazing material support is brought into contact with the repair portion, so that the brazing material is melted by said heating.
3. The method of repair according to claim 1 , wherein the porous material has flexibility.
4. The method of repair according to claim 1 , wherein after the brazing material has been solidified, the brazing material support is left to constitute a portion of the base.
5. The method of repair according to claim 1 , further comprising removing a removal portion of the base, and the brazing material support is placed at the portion of the base which portion has been subjected to the removal.
6. The method of repair according to claim 5 , wherein the repair portion has a crack which is removed by removing the removal portion of the base.
7. The method of repair according to claim 5 , wherein the molten brazing material is solidified when an exchange component to be exchanged with the removed portion of the base is brought into contact with the brazing material support, and thus, the base and the exchange component are bonded to each other through the brazing material support.
8. The method of repair according to claim 2 , wherein the porous material has flexibility.
9. The method of repair according to claim 2 , wherein after the brazing material has been solidified, the brazing material support is left to constitute a portion of the base.
10. The method of repair according to claim 2 , further comprising removing a removal portion of the base, and the brazing material support is placed at the portion of the base which portion has been subjected to the removal.
11. The method of repair according to claim 10 , wherein the repair portion has a crack which is removed by removing the removal portion of the base.
12. The method of repair according to claim 10 , wherein the molten brazing material is solidified when an exchange component to be exchanged with the removed portion of the base is brought into contact with the brazing material support, and thus, the base and the exchange component are bonded to each other through the brazing material support.