Rare earth-type tape-shaped oxide superconductor and a composite substrate used for the same
View Patent ↗This invention provides a rare earth-type tape-shaped oxide superconductor having excellent mechanical strength and superconducting properties and a composite substrate using for the same. Non-oriented and non-magnetic Ni-9 at % W alloy tapes ( 11, 21 ) were bonded onto both sides of a non-oriented and non-magnetic hastelloy tape ( 100 ) by a normal temperature bonding process, and an Ni-3 at % W alloy tape ( 12 ) having a cubic texture was bonded onto the surface of the tape ( 11 ) by a normal temperature bonding process. Thereafter, the heat-treatment was given in a reducing atmosphere and a bonding layer ( 50 a ) etc. was formed on the adhesive interface of each layer. Next, a (Ce, Gd)O 2 intermediate layer ( 13 ) and a Ce 2 Zr 2 O 7 intermediate layer ( 14 ) by an MOD process, a CeO 2 intermediate layer ( 15 ), a YBCO superconducting film ( 16 ) by a TFA-MOD method, and a silver stabilization layer ( 17 ) were stacked sequentially on the surface of the tape ( 12 ). A critical current value (Ic) of this superconductor showed 150 A.
1. A rare earth-type tape-shaped oxide superconductor, comprising:
a composite substrate comprising a metal substrate which is formed of non-oriented and non-magnetic metal, a first metal layer, and a second metal layer, said first and second metal layers being respectively bonded to opposing surfaces of said metal substrate through a first bonding layer and a second bonding layer, respectively;
at least one intermediate layer of a biaxially-oriented inorganic material formed on a surface of said first metal layer of said composite substrate; and
a rare earth oxide superconductive layer formed on said intermediate layer;
wherein the first and second bonding layers are formed by surface activated bonding at normal temperature, followed by a heat-treatment or hot rolling,
wherein said first metal layer comprises plural layers mutually bonded by surface activated bonding, followed by a heat-treatment or hot rolling,
wherein said first metal layer has first and second opposing surfaces,
wherein said first surface of said first metal layer faces said intermediate layer,
wherein said second surface of said first metal layer is bonded to said metal substrate through said second bonding layer,
wherein at least said first surface of said first metal layer has a biaxially-oriented cubic texture, and
wherein said metal substrate has a larger mechanical strength than that of said first and second metal layers.
2. A rare earth-type tape-shaped oxide superconductor according to claim 1 ,
wherein the first metal layer and the second metal layer function to prevent deformation of the composite substrate and at least the first metal layer functions to prevent diffusion of an element from the metal substrate.
3. A rare earth-type tape-shaped oxide superconductor according to claim 1 ,
wherein the metal substrate comprises a nickel-base alloy or a stainless steel.
4. A rare earth-type tape-shaped oxide superconductor according to claim 3 ,
wherein the metal substrate comprises a nickel-base alloy comprising nickel and one or more alloying elements selected from tungsten, molybdenum, chromium, iron, cobalt, vanadium and manganese.
5. A rare earth-type tape-shaped oxide superconductor according to claim 4 ,
wherein the first metal layer and the second metal layer comprise a nickel-base alloy comprising nickel and one or more alloying elements selected from tungsten, molybdenum, chromium, iron, cobalt, vanadium, manganese, copper and silver.
6. A rare earth-type tape-shaped oxide superconductor according to claim 1 ,
wherein the first metal layer comprises a nickel-base alloy comprising nickel and one or more alloying elements selected from tungsten, molybdenum, chromium, iron, cobalt, vanadium, manganese, copper and silver, and
wherein an additive amount of the alloying elements in the nickel-base alloy of each layer reduces gradually toward the intermediate layer from the first bonding layer.
7. A rare earth-type tape-shaped oxide superconductor according to claim 6 ,
wherein the additive amount of the alloying elements in the nickel-base alloy is within a range that a magnetic property of the nickel-base alloy disappears in at least the layer which contacts the first bonding layer, and is added within a range that a cubic texture of the nickel-base alloy is formed easily in at least the layer which contacts the intermediate layer.
8. A rare earth-type tape-shaped oxide superconductor according to claim 7 ,
wherein the additive amount of the alloying elements in the nickel-base alloy exceeds 8 at % in at least the layer which contacts the first bonding layer, and is less than 6 at % in at least the layer which contacts the intermediate layer.
9. A composite substrate for a rare earth-type tape-shaped oxide superconductor, comprising:
a metal substrate which is formed of non-oriented and non-magnetic metal; and
a first metal layer and a second metal layer which are respectively bonded to opposing surfaces of said metal substrate through a first bonding layer and a second bonding layer, respectively; and
wherein the first and second bonding layers are formed by surface activated bonding at normal temperature, followed by a heat-treatment or hot rolling,
wherein the first and second bonding layers are formed by surface activated bonding at normal temperature, followed by a heat-treatment or hot rolling,
wherein said first metal layer comprises plural layers mutually bonded by surface activated bonding, followed by a heat-treatment or hot rolling,
wherein said first metal layer has first and second opposing surfaces,
wherein at least said first surface of said first metal layer has a biaxially-oriented cubic texture,
wherein said second surface of said first metal layer is bonded to said metal substrate through said second bonding layer, and
wherein said metal substrate has a larger mechanical strength than that of said first and second metal layers.
10. A composite substrate for a rare earth-type tape-shaped oxide superconductor, comprising:
a metal substrate which is formed of non-oriented and non-magnetic metal; and
a first metal layer and a second metal layer which are respectively bonded to opposing surfaces of said metal substrate through a first bonding layer and a second bonding layer, respectively, and which function to prevent deformation of the composite substrate; and
wherein the first and second bonding layers are formed by surface activated bonding at normal temperature, followed by a heat-treatment or hot rolling,
wherein said first metal layer is formed of plural layers and functions to prevent diffusion of an element from said metal substrate,
wherein said plural layers of said metal layer are mutually bonded surface activated bonding, followed by a heat-treatment or hot rolling,
wherein said first metal layer has first and second opposing surfaces,
wherein at least said first surface of said first metal layer has a biaxially-oriented cubic texture,
wherein said second surface of said first metal layer is bonded to said metal substrate through said second bonding layer, and
wherein said metal substrate has a larger mechanical strength than that of said first and second metal layers.
11. A composite substrate for a rare earth-type tape-shaped oxide superconductor according to claim 10 ,
wherein the metal substrate, the first metal layer and the second metal layer comprise a nickel-base alloy.
12. A composite substrate for a rare earth-type tape-shaped oxide superconductor according to claim 11 ,
wherein the plural layers of the first metal layer are formed of the nickel-base alloy and wherein an additive amount of an element alloying with the nickel reduces gradually toward an outermost layer, among the plural layers, from a layer which contacts the first bonding layer.
13. A composite substrate for a rare earth-type tape-shaped oxide superconductor according to claim 12 ,
wherein the additive amount of the alloy elements in the nickel-base alloy exceeds 8 at % in at least the layer, among the plural layers, which contacts the first bonding layer, and is less than 6 at % in at least the outermost layer among the plural layers.
14. A composite substrate for a rare earth-type tape-shaped oxide superconductor according to claim 9 ,
wherein the metal substrate, the first metal layer and the second metal layer comprise a nickel-base alloy.